High efficiency dye-sensitized solar cell based on a novel gel polymer electrolyte containing RbI and tetrahexylammonium iodide (Hex4NI) salts and multi-layered photoelectrodes of TiO2 nanoparticles

T.M.W.J. Bandara, L. Ajith DeSilva, J.L. Ratnasekera, K.H. Hettiarachchi, A.P. Wijerathna, Madhavi Thakurdesai, Joshua Preston, I. Albinsson and B.-E. Mellander

Renewable and Sustainable Energy Reviews, 2019, vol. 103, issue C, 282-290

Abstract: High efficiency dye sensitized solar cells (DSSCs) have been achieved using a novel polymer gel electrolyte containing RbI and tetrahexylammonium iodide (Hex4NI) binary salts in combination with multi-layered TiO2 photoelectrodes. Performance enhancers were incorporated to the electrolyte to improve the efficiency in the DSSCs. Varying the salt mass fraction, showed that the conductivity in the electrolyte increases with increasing amount of RbI. The highest ionic conductivity of 4.19 mS cm−1 is exhibited by the electrolyte sample with RbI:Hex4NI weight ratio of 3:1 at 25 °C. The temperature dependence of the electrolytes shows Arrhenius behavior. It is found that the electrolyte with RbI:Hex4NI weight ratio of 1.06:1 is more suitable for DSSC's applications and it has a conductivity of 3.77 mS cm−1. A colloidal suspension of P25 TiO2 nanoparticles was used to make the spin coated photo-anodes in the form of stacks of 1–6 layers. The formation of a highly uniform and porous structure is observed with increasing number of layers from scanning electron microscopy and X-ray diffraction studies revealed that the layers are predominantly anatase phase with crystallite size of 19–22 nm. The band gap was estimated to be around 3.22 eV based on UV–Visible spectroscopy and found to be decreasing slightly with increasing layer thickness. The maximum efficiency of 7.5% and an impressively high current density of 20 mA cm−2 were observed for the 4-layer device with the new gel electrolyte based on RbI and Hex4NI. This study not only brings reliability and consistency to the ways of preparing well-ordered TiO2 photo-anodes but also offers the possibility of low-cost practical and highly efficient quasi-solid state DSSCs.

Keywords: Dye sensitized solar cells; TiO2 nanoparticles; P25; Spin coating; Multilayer DSSC; Binary salt; RbI and Tetrahexylammonium Iodide (search for similar items in EconPapers)
Date: 2019
References: View references in EconPapers View complete reference list from CitEc
Citations: View citations in EconPapers (2)

Downloads: (external link)
http://www.sciencedirect.com/science/article/pii/S1364032118308542
Full text for ScienceDirect subscribers only

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:eee:rensus:v:103:y:2019:i:c:p:282-290

Ordering information: This journal article can be ordered from
http://www.elsevier.com/wps/find/journaldescription.cws_home/600126/bibliographic
http://www.elsevier. ... 600126/bibliographic

DOI: 10.1016/j.rser.2018.12.052

Access Statistics for this article

Renewable and Sustainable Energy Reviews is currently edited by L. Kazmerski

More articles in Renewable and Sustainable Energy Reviews from Elsevier
Bibliographic data for series maintained by Catherine Liu ().