Technical Problem Identification for the Failures of the Liberty Ships

Wei Zhang
Additional contact information
Wei Zhang: Mine Management Division, Department of Mining & Mineral Resources, Chinalco China Copper Corporation Limited, Beijing 100082, China

Challenges, 2016, vol. 7, issue 2, 1-8

Abstract: The U.S. Liberty Ship Building Program in World War II set a record—a total of 2700 Liberty Ships were built in 6 years, in order to support the battle against Nazi-Germany. However, numerous vessels suffered sudden fracture, some of them being split in half. This paper demonstrates and investigation of the Liberty Ships failure and problems, which reveals that the failures are caused by a combination of three factors. The welds produced by largely unskilled work force contain crack type flaws. Beyond these cracks, another important reason for failure associated with welding is the hydrogen embitterment; most of the fractures initiate at deck square hatch corners where there is a stress concentration; and the ship steel has fairly poor Charpy-Impact tested fracture toughness. It has been admitted that, although the numerous catastrophic failures were a painful experience, the failures of the Liberty Ships caused significant progress in the study of fracture mechanics. Considering their effect, the Liberty Ships are still a success.

Keywords: Liberty Ship; fracture mechanics; propagating crack; material toughness (search for similar items in EconPapers)
JEL-codes: A00 C00 Z00 (search for similar items in EconPapers)
Date: 2016
References: View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.mdpi.com/2078-1547/7/2/20/pdf (application/pdf)
https://www.mdpi.com/2078-1547/7/2/20/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jchals:v:7:y:2016:i:2:p:20-:d:82316

Access Statistics for this article

Challenges is currently edited by Ms. Karen Sun

More articles in Challenges from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().