Computationally Modelling the Use of Nanotechnology to Enhance the Performance of Thermoelectric Materials

Peter Spriggs and Qing Wang
Additional contact information
Peter Spriggs: Department of Engineering, Durham University, Durham DH1 3LE, UK
Qing Wang: Department of Engineering, Durham University, Durham DH1 3LE, UK

Energies, 2020, vol. 13, issue 19, 1-21

Abstract: The increased focus on global climate change has meant that the thermoelectric market has received considerably more attention. There are many processes producing large amounts of waste heat that can be utilised to generate electrical energy. Thermoelectric devices have long suffered with low efficiencies, but this can be addressed in principle by improving the performance of the thermoelectric materials these devices are manufactured with. This paper investigates the thermoelectric performance of market standard thermoelectric materials before analysing how this performance can be improved through the adoption of various nanotechnology techniques. This analysis is carried out through the computational simulation of the materials over low-, mid- and high-temperature ranges. In the low-temperature range, through the use of nanopores and full frequency phonon scattering, Mg 0.97 Zn 0.03 Ag 0.9 Sb 0.95 performed best with a ZT value of 1.45 at 433 K. Across the mid-temperature range a potentially industry leading ZT value of 2.08 was reached by AgSbTe 1.85 Se 0.15 . This was carried out by simulating the effect of band engineering and the introduction of dense stacking faults due to the addition of Se into AgSbTe 2 . AgSbTe 1.85 Se 0.15 cannot be implemented in devices operating above 673 K because it degrades too quickly. Therefore, for the top 200 K of the mid-temperature range a PbBi 0.002 Te–15% Ag 2 Te nanocomposite performed best with a maximum ZT of 2.04 at 753 K and maximum efficiency of 23.27 at 813 K. In the high-temperature range, through the doping of hafnium (Hf) the nanostructured FeNb 0.88 Hf 0.12 Sb recorded the highest ZT value of 1.49 at 1273 K. This was closely followed by Fe 1.05 Nb 0.75 Ti 0.25 Sb, which recorded a ZT value of 1.31 at 1133 K. This makes Fe 1.05 Nb 0.75 Ti 0.25 Sb an attractive substitute for FeNb 0.88 Hf 0.12 Sb due to the much lower cost and far greater abundance of titanium (Ti) compared with hafnium.

Keywords: COMSOL; Seebeck coefficient; thermoelectric effect; ZT (search for similar items in EconPapers)
JEL-codes: Q Q0 Q4 Q40 Q41 Q42 Q43 Q47 Q48 Q49 (search for similar items in EconPapers)
Date: 2020
References: View references in EconPapers View complete reference list from CitEc
Citations: View citations in EconPapers (1)

Downloads: (external link)
https://www.mdpi.com/1996-1073/13/19/5096/pdf (application/pdf)
https://www.mdpi.com/1996-1073/13/19/5096/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jeners:v:13:y:2020:i:19:p:5096-:d:421943

Access Statistics for this article

Energies is currently edited by Ms. Agatha Cao

More articles in Energies from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().