CH 4 Adsorption in Wet Metal-Organic Frameworks under Gas Hydrate Formation Conditions Using A Large Reactor

Jyoti Shanker Pandey (), Nehir Öncü and Nicolas von Solms
Additional contact information
Jyoti Shanker Pandey: Center for Energy Resource Engineering (CERE), Department of Chemical Engineering, Technical University of Denmark, 2800 Kongens Lyngby, Denmark
Nehir Öncü: Center for Energy Resource Engineering (CERE), Department of Chemical Engineering, Technical University of Denmark, 2800 Kongens Lyngby, Denmark
Nicolas von Solms: Center for Energy Resource Engineering (CERE), Department of Chemical Engineering, Technical University of Denmark, 2800 Kongens Lyngby, Denmark

Energies, 2024, vol. 17, issue 14, 1-23

Abstract: Nanoporous materials, such as metal-organic frameworks (MOFs), are renowned for their high selectivity as gas adsorbents due to their specific surface area, nanoporosity, and active surface chemistry. A significant challenge for their widespread application is reduced gas uptake in wet conditions, attributed to competitive adsorption between gas and water. Recent studies of gas adsorption in wet materials have typically used small amounts of powdered porous materials (in the milligram range) within very small reactors (1–5 mL). This leaves a gap in knowledge about gas adsorption behaviors in larger reactors and with increased MOF sample sizes (to the gram scale). Additionally, there has been a notable absence of experimental research on MOFs heavily saturated with water. In this study, we aimed to fill the gaps in our understanding of gas adsorption in wet conditions by measuring CH 4 adsorption in MOFs. To do this, we used larger MOF samples (in grams) and a large-volume reactor. Our selection of commercially available MOFs, including HKUST-1, ZIF-8, MOF-303, and activated carbon, was based on their widespread application, available previous research, and differences in hydrophobicity. Using a volumetric approach, we measured high-pressure isotherms (at T = 274.15 K) to compare the moles of gas adsorbed under both dry and wet conditions across different MOFs and weights. The experimental results indicate that water decreases total CH 4 adsorption in MOFs, with a more pronounced decrease in hydrophilic MOFs compared to hydrophobic ones at lower pressures. However, hydrophilic MOFs exhibited stepped isotherms at higher pressures, suggesting water converts to hydrate, positively impacting total gas uptake. In contrast, the hydrophobic ZIF-8 did not promote hydrate formation due to particle aggregation in the presence of water, leading to a loss of surface area and surface charge. This study highlights the additional challenges associated with hydrate-MOF synergy when experiments are scaled up and larger sample sizes are used. Future studies should consider using monolith or pellet forms of MOFs to address the limitations of powdered MOFs in scale-up studies.

Keywords: metal-organic framework; high-pressure isotherms; gas hydrates; CH 4 storage (search for similar items in EconPapers)
JEL-codes: Q Q0 Q4 Q40 Q41 Q42 Q43 Q47 Q48 Q49 (search for similar items in EconPapers)
Date: 2024
References: View references in EconPapers View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.mdpi.com/1996-1073/17/14/3509/pdf (application/pdf)
https://www.mdpi.com/1996-1073/17/14/3509/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jeners:v:17:y:2024:i:14:p:3509-:d:1436943

Access Statistics for this article

Energies is currently edited by Ms. Agatha Cao

More articles in Energies from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().