Optimizing S Chemical Looping Combustion with Cu-Fe Combined Oxygen Carriers: Performance and Mechanistic Insights

Lihuai Peng and Min Zheng ()
Additional contact information
Lihuai Peng: School of Metallurgy and Energy Engineering, Kunming University of Science and Technology, Kunming 650093, China
Min Zheng: School of Metallurgy and Energy Engineering, Kunming University of Science and Technology, Kunming 650093, China

Energies, 2024, vol. 17, issue 20, 1-21

Abstract: This study focuses on the S-to-H 2 SO 4 industry by investigating the chemical looping combustion (CLC) process utilizing Fe-based and Cu-based oxygen carriers (OCs), which are widely applied in CLC technology. The primary objective is to conduct combined CLC reactions of these two metal carriers in a three-zone temperature tube furnace, aiming to achieve a higher SO 2 yield than what is attainable by reacting a single metal carrier with S. The investigation reveals promising industrial applications, offering potential benefits in terms of reducing equipment costs, enhancing energy efficiency, and lowering the emissions of the H 2 SO 4 production industry. Through a series of experiments, the study examines the effects of reaction temperature and material molar ratios on SO 2 generation. The solid reaction products were characterized using X-ray diffraction (XRD), scanning electron microscopy with energy-dispersive spectroscopy (SEM-EDS), and X-ray photoelectron spectroscopy (XPS). The experimental results indicate that the combined Cu-based and Fe-based OCs exhibit a higher SO 2 yield during the reduction stage compared to using either Fe-based or Cu-based OCs independently. Under optimal conditions, with a carrier gas flow rate of 300 mL/min, an Fe 2 O 3 /S molar ratio of 6:1 in the second temperature zone, and a reaction temperature of 900 °C, the total SO 2 yield in the third temperature zone reached approximately 85%. This was achieved at a reaction temperature of 850 °C, with an Fe 2 O 3 /S molar ratio of 6:1 in the first half of the zone and a CuO/S molar ratio of 12:1 in the second half of the zone. SEM-EDS analysis further revealed that the combined OCs showed no significant signs of agglomeration or sintering after 10 cycles of the reaction. However, Cu-based carrier particles increased in size by 50%, while Fe-based carrier particles remained relatively stable. Additionally, the low mass-to-atom ratio of S on the surface of OCs after the cyclic reaction suggests that the reduced-state OCs can be fully oxidized and regenerated following the release of SO 2 during oxidation.

Keywords: chemical looping combustion; Cu-based oxygen carrier; Fe-based oxygen carrier; S; SO 2 (search for similar items in EconPapers)
JEL-codes: Q Q0 Q4 Q40 Q41 Q42 Q43 Q47 Q48 Q49 (search for similar items in EconPapers)
Date: 2024
References: View references in EconPapers View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.mdpi.com/1996-1073/17/20/5018/pdf (application/pdf)
https://www.mdpi.com/1996-1073/17/20/5018/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jeners:v:17:y:2024:i:20:p:5018-:d:1495229

Access Statistics for this article

Energies is currently edited by Ms. Agatha Cao

More articles in Energies from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().