Dry–Wet Cyclic Sulfate Attack Mechanism of High-Volume Fly Ash Self-Compacting Concrete

Junxia Liu (), Anbang Li, Yanmeng Yang, Xueping Wang and Fei Yang ()
Additional contact information
Junxia Liu: School of Architectural Engineering, Zhongyuan University of Technology, Zhengzhou 450007, China
Anbang Li: School of Architectural Engineering, Zhongyuan University of Technology, Zhengzhou 450007, China
Yanmeng Yang: School of Architectural Engineering, Zhongyuan University of Technology, Zhengzhou 450007, China
Xueping Wang: School of Materials Science and Engineering, Tianjin Chengjian University, Tianjin 300384, China
Fei Yang: School of Architectural Engineering, Zhongyuan University of Technology, Zhengzhou 450007, China

Sustainability, 2022, vol. 14, issue 20, 1-13

Abstract: High-volume fly ash replacing cement helps to improve the fluidity, volume stability, durability, and economy of self-compacting concrete (SCC). Sulfate attack is the most common form of the durability damage of hydraulic concrete; in particular, the performance degradation at the water level change position is more significant. Therefore, research on the influence effect and mechanism of fly ash on the durability is of great significance. In this paper, the change regularity of the SCC physical and mechanical properties with the fly ash replacement percentage and dry–wet cycles were studied by 60 dry–wet cycles of sulfate attack test. The 6 h electric flux, MIP, and SEM were used to study the performance degradation mechanism of SCC cured for 56 days, which had also been attacked by sulfate. The results show that the physical and mechanical properties of SCC increased first and then decreased with the dry–wet cycles of sulfate attack. After 10–15 cycles, the corresponding properties increased slightly, and then decreased gradually. When the fly ash content was 40%, the corrosion resistance coefficient, relative dynamic elastic modulus, and flexural strength retention were higher than those of the control specimen. However, when the fly ash content was 50%, they were close to the control and deteriorated obviously with the further addition of fly ash. For pore sizes in the range of 120–1000 nm, the porosity of SCC cured for 56 days was inversely proportional to the 6 h electric flux and the retention of mechanical properties, indicating that the porosity of the large pores is the decisive factor affecting the chloride ion permeability and corrosion resistance. The incorporation of fly ash in SCC can change the sulfate attack products and destruction mechanism. The sulfate attack damage of SCC with 40% of fly ash and the control specimen was dominated by ettringite crystallization and expansion, while those with a fly ash content of 50% and 60% had no obvious corrosion products, and the microstructures became looser. The appropriate fly ash replacement percentage could significantly improve the corrosion resistance of SCC.

Keywords: dry–wet cycle; electric flux; fly ash; porosity; self-compacting concrete; sulfate attack (search for similar items in EconPapers)
JEL-codes: O13 Q Q0 Q2 Q3 Q5 Q56 (search for similar items in EconPapers)
Date: 2022
References: View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.mdpi.com/2071-1050/14/20/13052/pdf (application/pdf)
https://www.mdpi.com/2071-1050/14/20/13052/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jsusta:v:14:y:2022:i:20:p:13052-:d:939917

Access Statistics for this article

Sustainability is currently edited by Ms. Alexandra Wu

More articles in Sustainability from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().