Blending Plastics Waste with Highly Available Jordanian Kaolin for Preparation of Alkali-Activated Mortars

Mohamed El-Tanani, Bassam Z. Mahasneh, Faryza Muhana (), Bassam El-Eswed, Fawwaz Khalili and Tariq Alkhrissat
Additional contact information
Mohamed El-Tanani: Phamacological and Diagnostic Research Center (PDRC), Faculty of Pharmacy, Al-Ahliyya Amman University, Amman 19328, Jordan
Bassam Z. Mahasneh: Faculty of Engineer, Al al-Bayt University, Mafraq 130040, Jordan
Faryza Muhana: Phamacological and Diagnostic Research Center (PDRC), Faculty of Pharmacy, Al-Ahliyya Amman University, Amman 19328, Jordan
Bassam El-Eswed: Zarqa College, Al-Balqa Applied University, Zarqa 13110, Jordan
Fawwaz Khalili: Department of Chemistry, School of Science, The University of Jordan, Amman 11942, Jordan
Tariq Alkhrissat: Faculty of Engineer, Al-Ahliyya Amman University, Amman 19328, Jordan

Sustainability, 2022, vol. 14, issue 23, 1-15

Abstract: Due to their lower energy demand, alkali-activated materials or geopolymers (GPs) are strong candidates to replace ordinary Portland cement binders in some applications. The present article attempts to investigate the possibility of incorporating plastics waste in place of silica sand filler in the GP mortars. The compressive strength, density, FTIR, XRD, BET and SEM of the prepared mortars were evaluated. Satisfactory compressive strength was achieved for metakaolin (MK)-based GP mortars containing plastic fillers (polyvinylchloride (PV), polystyrene (PS), polypropylene (PP) and polyethylene (PE)) which was dependent on the nature of plastic incorporated in the GP matrix: MKPV (30.3 MPa) > MKPS (15.8 MPa)~MKPP (15.9 MPa) > MKPE (9.1 MPa). The 28-day compressive strength of GP containing polyvinyl chloride was almost equivalent to that containing silica sand. Much lower values were obtained for the corresponding kaolin-based GPs (2.5, 2.8, 1.8 and 2.2 MPa, respectively). As reflected by FTIR absorption bands at 1447 and 1400 cm −1 , the addition of plastic filler reduces absorption of CO 2 from the atmosphere which enhanced dissolution of Al species from metakaolin. The morphology of GPs containing plastic fillers exhibited amorphous tissue-like structure compared to crystalline structure in the case of GP containing silica sand. However, both types of GPs exhibited lower porosity than previously prepared metakaolin-based GPs. Remarkably, poor adhesion of plastic filler to the GP binder was observed due to the inertness of plastic fillers toward alkali activators.

Keywords: geopolymer; Jordanian kaolin; metakaolin; plastic waste; alkali-activated materials (search for similar items in EconPapers)
JEL-codes: O13 Q Q0 Q2 Q3 Q5 Q56 (search for similar items in EconPapers)
Date: 2022
References: View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.mdpi.com/2071-1050/14/23/15742/pdf (application/pdf)
https://www.mdpi.com/2071-1050/14/23/15742/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jsusta:v:14:y:2022:i:23:p:15742-:d:984792

Access Statistics for this article

Sustainability is currently edited by Ms. Alexandra Wu

More articles in Sustainability from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().