Comparative Analysis of Hotspot Stress Endurance in Pristine and Thermal Cycled Prestressed Glass–Glass Photovoltaic Modules

Muhammad Afridi (), Akash Kumar, Farrukh ibne Mahmood and GovindaSamy TamizhMani
Additional contact information
Muhammad Afridi: Photovoltaic Reliability Laboratory, Arizona State University, Mesa, AZ 85212, USA
Akash Kumar: Photovoltaic Reliability Laboratory, Arizona State University, Mesa, AZ 85212, USA
Farrukh ibne Mahmood: Photovoltaic Reliability Laboratory, Arizona State University, Mesa, AZ 85212, USA
GovindaSamy TamizhMani: Photovoltaic Reliability Laboratory, Arizona State University, Mesa, AZ 85212, USA

Sustainability, 2023, vol. 15, issue 16, 1-16

Abstract: Hotspots pose a significant long-term reliability challenge in photovoltaic (PV) modules that can have a detrimental impact on the efficiency, safety, and financial viability of a PV system. This paper aims to evaluate the endurance of hotspot stress in pristine and prestressed glass–glass (GG) modules. The accelerated prestressing was conducted for 600 thermal cycles (TC600) to represent decades of field exposure. GG modules are quickly becoming an alternative to the traditional glass–backsheet (GB) modules that have been the industry standard. Unlike other conventional studies that subject only pristine modules to hotspot stress, this paper evaluates the performance of an accelerated/simulated field-aged GG module (using TC600) and a pristine GG module. Pre- and post-characterizations were performed before and after each test to determine changes in electrical performance and observe any defects in GG modules. During the hotspot test, an approximately 200 °C maximum cell temperature was observed with a cell shading of 25% (the worst-case shading ratio). After the hotspot test, electroluminescence imaging indicated that most cells in the prestressed GG module exhibited severe damage whereas no significant defects were evident in the pristine GG module where the prestressed GG module degraded 8.2% and the pristine GG module degraded 1.5% in maximum power. These findings are critical for the industry, considering that GG bifacial modules will dominate the market.

Keywords: accelerated life test (ALT); thermal cycling; glass–glass module; full-cells; photovoltaic (PV); hotspot (search for similar items in EconPapers)
JEL-codes: O13 Q Q0 Q2 Q3 Q5 Q56 (search for similar items in EconPapers)
Date: 2023
References: View references in EconPapers View complete reference list from CitEc
Citations: View citations in EconPapers (1)

Downloads: (external link)
https://www.mdpi.com/2071-1050/15/16/12131/pdf (application/pdf)
https://www.mdpi.com/2071-1050/15/16/12131/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jsusta:v:15:y:2023:i:16:p:12131-:d:1212962

Access Statistics for this article

Sustainability is currently edited by Ms. Alexandra Wu

More articles in Sustainability from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().