Fabrication of Novel Polymer Composites from Leather Waste Fibers and Recycled Poly(Ethylene-Vinyl-Acetate) for Value-Added Products

Shubham Sharma, P. Sudhakara, Jujhar Singh, Sanjay M. R. () and S. Siengchin
Additional contact information
Shubham Sharma: CSIR—Central Leather Research Institute, Regional Centre, Jalandhar 144021, Punjab, India
P. Sudhakara: CSIR—Central Leather Research Institute, Regional Centre, Jalandhar 144021, Punjab, India
Jujhar Singh: Department of Mechanical Engineering, IK Gujral Punjab Technical University, Jalandhar-Kapurthala Road, Kapurthala 144603, Punjab, India
Sanjay M. R.: Natural Composites Research Group Lab., Department of Materials and Production Engineering, The Sirindhorn International Thai-German Graduate School of Engineering (TGGS), King Mongkut’s University of Technology North Bangkok (KMUTNB), Bangkok 10800, Thailand
S. Siengchin: Natural Composites Research Group Lab., Department of Materials and Production Engineering, The Sirindhorn International Thai-German Graduate School of Engineering (TGGS), King Mongkut’s University of Technology North Bangkok (KMUTNB), Bangkok 10800, Thailand

Sustainability, 2023, vol. 15, issue 5, 1-50

Abstract: This investigation was focused on evaluating the utilization of Leather-waste, i.e., “Leather Shavings”, to develop “Poly(ethylene-vinyl-acetate)” (EVA) based “polymer matrix composites”. Composites with the highest ratio of 1:1 were developed using a rolling-mill, which was then subjected to hot-press molding for value-added applications, notably in the “floor-covering”, “structural”, “footwear”, and “transportation domain”. The specimens were examined for evaluating the “physico-mechanical characteristics” such as, “Compressive and Tensile, strength, Abrasion-resistance, Density, tear-resistance, hardness, adhesion-strength, compression, and resilience, damping, and water absorption” as per standard advanced testing techniques. Raising the leather-fiber fraction in the composites culminated in considerable enhancement in “physico-mechanical characteristics” including “modulus”, and a decline in “tensile-strain” at “fracture-breakage”. The thermo-analytic methods, viz. TGA and DSC studies have evidenced that substantial enhancement of thermo-stability (up to 211.1–213.81 °C) has been observed in the newly developed PMCs. Additionally, the DSC study showed that solid leather fibers lose water at an endothermic transition temperature of around 100 °C, are thermo-stable at around 211 degrees centigrade, and begin to degrade at 332.56-degree centigrade for neat recycled EVA samples and begin to degrade collagen at 318.47-degree centigrade for “leather shavings/recycled EVA polymer composite samples”, respectively. Additionally, the “glass transition temperature” (T g ) of the manufactured composites was determined to be between −16 and 30 °C. Furthermore, SEM and EDAX analysis have been used to investigate the morphological characteristics of the developed composites. Micrograph outcomes have confirmed the excellent “uniformity, compatibility, stability and better-bonding” of leather-fibers within the base matrix. Additionally, the “Attenuated-total-reflection” (ATR-FTIR) was carried out to test the “physicochemical chemical-bonding”, “molecular-structure”, and “functional-groups” of the “base matrix”, and its “composites” further affirm the “recycled EVA matrix” contained additives remain within the polymeric-matrix. An “X-ray diffraction study” was also conducted to identify the “chemical-constituents” or “phases” involved throughout the “crystal-structures” of the base matrix and PMCs. Additionally, AFM analysis has also been utilized to explore the “interfacial adhesion properties” of mechanically tested specimens of fabricated polymeric composite surfaces, their “surface topography mapping”, and “phase-imaging analysis” of polymer composites that have leather-shavings fibers.

Keywords: leather shavings; recycled EVA; compression molding; rolling; footwear and leather ancillaries(s) applications (search for similar items in EconPapers)
JEL-codes: O13 Q Q0 Q2 Q3 Q5 Q56 (search for similar items in EconPapers)
Date: 2023
References: View references in EconPapers View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.mdpi.com/2071-1050/15/5/4333/pdf (application/pdf)
https://www.mdpi.com/2071-1050/15/5/4333/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jsusta:v:15:y:2023:i:5:p:4333-:d:1083744

Access Statistics for this article

Sustainability is currently edited by Ms. Alexandra Wu

More articles in Sustainability from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().