Effects of Different Silicon Sources on the Properties of Geopolymer Planting Concrete Mixed with Red Mud

Wei Chen and Jiusu Li ()
Additional contact information
Wei Chen: School of Traffic and Transportation Engineering, Changsha University of Science & Technology, Changsha 410114, China
Jiusu Li: School of Traffic and Transportation Engineering, Changsha University of Science & Technology, Changsha 410114, China

Sustainability, 2023, vol. 15, issue 5, 1-21

Abstract: In order to reduce the carbon emission of planting concrete in the process of preparation, and to realize the application of large amounts of red mud in the geopolymer, in this study, high silicon source materials and blast furnace slag are added to a large content of red mud base geopolymer planting concrete, which can remove the dependence of planting concrete on ordinary Portland cement and provide a new direction for the comprehensive utilization of red mud. In the paper, the effects of different A (Alkali solid content)/P (Powder dosage) and high silica sources (silica fume and diatomite) on the microstructure and fluidity of the geopolymer, as well as the compressive strength, pore characteristics, and alkalinity of the planting concrete, are comparatively evaluated. The corresponding results showed that when A/P was 0.25, the planting performance of the planting concrete would be reduced due to its high alkalinity; when A/P was 0.15, the planting concrete would have its sedimentation and the compressive strength decreased. On the other hand, the pozzolanic reaction among the silica fume, diatomite, and Ca(OH) 2 significantly weakened the alkali pan phenomenon in the later stage of planting concrete formation. The addition of an appropriate amount of silica fume and diatomite also made the structure of the geopolymer more compact with better fluidity, which yielded superior pore characteristics and planting performance for the planting concrete. For good planting concrete pore characteristics, the test results showed that the fluidity of the mortar should be 112–128 mm. Overall, the best planting concrete performance was achieved at an A/P ratio of 0.2, with the contents of silica fume and diatomite being 10% and 5%, respectively. Furthermore, the slope finite element analysis showed that planting concrete made with red mud geopolymer had better slope protection potential than ordinary Portland cement.

Keywords: red mud; silica fume (SF); diatomite (DA); geopolymer; planting concrete (PC) (search for similar items in EconPapers)
JEL-codes: O13 Q Q0 Q2 Q3 Q5 Q56 (search for similar items in EconPapers)
Date: 2023
References: View references in EconPapers View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.mdpi.com/2071-1050/15/5/4427/pdf (application/pdf)
https://www.mdpi.com/2071-1050/15/5/4427/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jsusta:v:15:y:2023:i:5:p:4427-:d:1085082

Access Statistics for this article

Sustainability is currently edited by Ms. Alexandra Wu

More articles in Sustainability from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().