Sustainability through Optimal Compositional and Thermomechanical Design for the Al-7XXX Alloys: An ANOVA Case Study

Muhammad Farzik Ijaz (), Basim T. Nashri () and Mansour T. Qamash
Additional contact information
Muhammad Farzik Ijaz: Mechanical Engineering Department, College of Engineering, King Saud University, P.O. Box 800, Riyadh 11421, Saudi Arabia
Basim T. Nashri: Mechanical Engineering Department, College of Engineering, King Saud University, P.O. Box 800, Riyadh 11421, Saudi Arabia
Mansour T. Qamash: Department of Mechanical Engineering, Marquette University, Milwaukee, WI 53233, USA

Sustainability, 2024, vol. 16, issue 4, 1-25

Abstract: The quest for lightweight, high-performance structural materials for demanding applications such as in the fields of automotive, aerospace, and other high-tech and military industries pushes the boundaries of material science. The present work aims to draw attention to a novel, sustainable manufacturing approach for the development of next-generation 7xxx series aluminum alloys that have higher strength by rejuvenating a sustainable compositional and thermomechanical processing strategy. Our innovative strategy integrates two key synergies: trace hafnium (Hf) addition for microstructural refinement, unique thermomechanical treatment involving cryorolling, and a short annealing method. Experimental results revealed that our base alloy exhibited a 33 µm grain size and impressive initial mechanical properties (334 MPa UTS, 150 HV). Adding 0.6 wt.% Hf and employing 50% cryorolling with short annealing led to a remarkable 10 µm grain size reduction and significant mechanical property leaps. The resulting alloy boasts a 452 MPa UTS and 174 HV, showcasing the synergistic advantageous effect of Hf and cryorolling plus annealing treatment. The developed alloys were compositional- and work hardening-dependent, leading to a rich mix of strengthening mechanisms. Optical and scanning electron microscopy reveal several intermetallic phases within the fcc matrix, wherein the Al 3 Hf phase plays a key role in strengthening by impeding dislocation movement. In addition to experimental results, a 12-full-factorial design experiment via ANOVA analysis was also utilized to validate the significant influence of Hf and cryorolling on properties with ( p -values < 0.05). Among the different parameters, cryorolling plus annealing appeared as the most noteworthy factor, followed by the composition. Using the regression model, the ultimate tensile strength and hardness were predicted to be 626 MPa UTS and 192 HV for an alloy with 0.6 wt.% Hf and 85% cryorolling, which opens a new avenue for ultra-high-strength Al7xxx alloys.

Keywords: cryorolling; Al-Zn-Mg-Cu alloy; hafnium; sustainable manufacturing; fine grain strengthening; Al 3 Hf; full-factorial design; ANOVA (search for similar items in EconPapers)
JEL-codes: O13 Q Q0 Q2 Q3 Q5 Q56 (search for similar items in EconPapers)
Date: 2024
References: View references in EconPapers View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.mdpi.com/2071-1050/16/4/1515/pdf (application/pdf)
https://www.mdpi.com/2071-1050/16/4/1515/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jsusta:v:16:y:2024:i:4:p:1515-:d:1337159

Access Statistics for this article

Sustainability is currently edited by Ms. Alexandra Wu

More articles in Sustainability from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().