Effect of Rebar Harsh Storage Conditions on the Flexural Behavior of Glass FRP Concrete

Sami W. Tabsh (), Adil Tamimi, Magdi El-Emam and Ali Zandavi
Additional contact information
Sami W. Tabsh: Department of Civil Engineering, College of Engineering, The American University of Sharjah, Sharjah P.O. Box 26666, United Arab Emirates
Adil Tamimi: Department of Civil Engineering, College of Engineering, The American University of Sharjah, Sharjah P.O. Box 26666, United Arab Emirates
Magdi El-Emam: Department of Civil Engineering, College of Engineering, The American University of Sharjah, Sharjah P.O. Box 26666, United Arab Emirates
Ali Zandavi: Qeyas Contracting L.L.C., Dubai P.O. Box 74956, United Arab Emirates

Sustainability, 2024, vol. 16, issue 5, 1-20

Abstract: Nowadays, fiber-reinforced polymer (FRP) has become a widely accepted alternative reinforcement to steel bars in concrete members due to its many sustainability traits, as represented by its high strength-to-weight ratio, corrosion resistance, non-conductive properties, and electromagnet neutrality. However, FRP bar exposure for an extended period of time to harsh environmental conditions and chemicals can have an adverse effect on their mechanical properties. In this investigation, glass FRP bars were exposed to indoor controlled temperature, outdoor direct sunlight, outdoor shade, seawater, and alkaline solution for six months prior to using them as reinforcement in concrete flexural members. This research involves the fabrication and testing of five pairs of 3 m-long concrete beams with 200 mm by 300 mm cross-sections embedded in the tension zone with the exposed GFRP bars. The 10 beams were instrumented with strain gauges and tested following a four-point loading scheme using a hydraulic jack attached to a rigid steel frame. Crack width records from the tests showed the inferior serviceability of the beams that contained rebars stored in an outdoor environment relative to the control beams. GFRP bar exposure to an alkaline solution or outdoor direct sunlight slightly affected the cracking and ultimate moment capacities, reducing them by 5% and 3% in terms of the same parameters as the controlled indoor exposure, respectively. The influence of GFRP bar exposure to open-air shade or sunlight decreased the pre-cracking stiffness by 25% and flexural ductility by 10–20% when compared with the control specimens. The predicted ultimate flexural strength using the ACI 440 provisions gave comparable results to the experimentally obtained values. A simple mathematical equation that envelops the moment–deflection relationship for GFRP over-reinforced concrete beams and only requires information about initial cracking and ultimate flexural conditions is proposed.

Keywords: composites; environmental exposure; flexure; glass-fiber-reinforced polymer; reinforced concrete; sustainability (search for similar items in EconPapers)
JEL-codes: O13 Q Q0 Q2 Q3 Q5 Q56 (search for similar items in EconPapers)
Date: 2024
References: View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.mdpi.com/2071-1050/16/5/1944/pdf (application/pdf)
https://www.mdpi.com/2071-1050/16/5/1944/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jsusta:v:16:y:2024:i:5:p:1944-:d:1346875

Access Statistics for this article

Sustainability is currently edited by Ms. Alexandra Wu

More articles in Sustainability from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().