Phase segregation due to ion migration in all-inorganic mixed-halide perovskite nanocrystals

Huichao Zhang, Xu Fu, Ying Tang, Hua Wang, Chunfeng Zhang, William W. Yu, Xiaoyong Wang (), Yu Zhang () and Min Xiao ()
Additional contact information
Huichao Zhang: Nanjing University
Xu Fu: Nanjing University
Ying Tang: Nanjing University
Hua Wang: Jilin University
Chunfeng Zhang: Nanjing University
William W. Yu: Jilin University
Xiaoyong Wang: Nanjing University
Yu Zhang: Jilin University
Min Xiao: Nanjing University

Nature Communications, 2019, vol. 10, issue 1, 1-8

Abstract: Abstract Semiconductor mixed-halide perovskites featured with a tunable energy bandgap are ideal candidates for light absorbers in tandem solar cells as well as fluorescent materials in light-emitting diodes and nanoscale lasers. These device advancements are currently hindered by the light-induced phase segregation effect, whereby ion migration would yield smaller-bandgap domains with red-shifted photoluminescence. Here we show that upon laser excitation all-inorganic mixed-halide nanocrystals unexpectedly exhibit a blue shift in the photoluminescence peak that can revert back in the dark, thus depicting the processes of ion migration out of and back to the originally excited nanocrystals. Interestingly, this reversible photoluminescence shift can also be induced by electrical biasing of mixed-halide nanocrystals without the injection of charge carriers. The above findings suggest that it is the local electric field that breaks the ionic bonds in mixed-halide nanocrystals, which could be a universal origin for light-induced phase segregation observed in other mixed-halide perovskite materials.

Date: 2019
References: Add references at CitEc
Citations: View citations in EconPapers (1)

Downloads: (external link)
https://www.nature.com/articles/s41467-019-09047-7 Abstract (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:nat:natcom:v:10:y:2019:i:1:d:10.1038_s41467-019-09047-7

Ordering information: This journal article can be ordered from
https://www.nature.com/ncomms/

DOI: 10.1038/s41467-019-09047-7

Access Statistics for this article

Nature Communications is currently edited by Nathalie Le Bot, Enda Bergin and Fiona Gillespie

More articles in Nature Communications from Nature
Bibliographic data for series maintained by Sonal Shukla () and Springer Nature Abstracting and Indexing ().

 
Page updated 2025-03-19
Handle: RePEc:nat:natcom:v:10:y:2019:i:1:d:10.1038_s41467-019-09047-7