Xinxin Wang, Jingjing Chen, Dajian Wang and Zhiyong Mao ()
Additional contact information
Xinxin Wang: Tianjin University of Technology
Jingjing Chen: Tianjin University of Technology, Ministry of Education
Dajian Wang: Tianjin University of Technology, Ministry of Education
Zhiyong Mao: Tianjin University of Technology

Nature Communications, 2021, vol. 12, issue 1, 1-8

Abstract: Abstract The combination of alkali metal electrodes and solid-state electrolytes is considered a promising strategy to develop high-energy rechargeable batteries. However, the practical applications of these two components are hindered by the large interfacial resistance and growth of detrimental alkali metal depositions (e.g., dendrites) during cycling originated by the unsatisfactory electrode/solid electrolyte contact. To tackle these issues, we propose a room temperature ultrasound solid welding strategy to improve the contact between Na metal and Na3Zr2Si2PO12 (NZSP) inorganic solid electrolyte. Symmetrical Na|NZSP | Na cells assembled via ultrasonic welding show stable Na plating/stripping behavior at a current density of 0.2 mA cm−2 and a higher critical current density (i.e., 0.6 mA cm−2) and lower interfacial impedance than the symmetric cells assembled without the ultrasonic welding strategy. The beneficial effect of the ultrasound welding is also demonstrated in Na|NZSP | Na3V2(PO4)3 full coin cell configuration where 900 cycles at 0.1 mA cm−2 with a capacity retention of almost 90% can be achieved at room temperature.

Date: 2021
References: View references in EconPapers View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.nature.com/articles/s41467-021-27473-4 Abstract (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:nat:natcom:v:12:y:2021:i:1:d:10.1038_s41467-021-27473-4

Ordering information: This journal article can be ordered from
https://www.nature.com/ncomms/

DOI: 10.1038/s41467-021-27473-4

Access Statistics for this article

Nature Communications is currently edited by Nathalie Le Bot, Enda Bergin and Fiona Gillespie

More articles in Nature Communications from Nature
Bibliographic data for series maintained by Sonal Shukla () and Springer Nature Abstracting and Indexing ().