Control of metal oxides’ electronic conductivity through visual intercalation chemical reactions

Yuanyuan Zhang, Xiaohua Zhang, Quanquan Pang and Jianhua Yan ()
Additional contact information
Yuanyuan Zhang: Donghua University
Xiaohua Zhang: Donghua University
Quanquan Pang: Peking University
Jianhua Yan: Donghua University

Nature Communications, 2023, vol. 14, issue 1, 1-11

Abstract: Abstract Cation intercalation is an effective method to optimize the electronic structures of metal oxides, but tuning intercalation structure and conductivity by manipulating ion movement is difficult. Here, we report a visual topochemical synthesis strategy to control intercalation pathways and structures and realize the rapid synthesis of flexible conductive metal oxide films in one minute at room temperature. Using flexible TiO2 nanofiber films as the prototype, we design three charge-driven models to intercalate preset Li+-ions into the TiO2 lattice slowly (µm/s), rapidly (mm/s), or ultrafast (cm/s). The Li+-intercalation causes real-time color changes of the TiO2 films from white to blue and then black, corresponding to the structures of LixTiO2 and LixTiO2-δ, and the enhanced conductivity from 0 to 1 and 40 S/m. This work realizes large-scale and rapid synthesis of flexible TiO2 nanofiber films with tunable conductivity and is expected to extend the synthesis to other conductive metal oxide films.

Date: 2023
References: View references in EconPapers View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.nature.com/articles/s41467-023-41935-x Abstract (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:nat:natcom:v:14:y:2023:i:1:d:10.1038_s41467-023-41935-x

Ordering information: This journal article can be ordered from
https://www.nature.com/ncomms/

DOI: 10.1038/s41467-023-41935-x

Access Statistics for this article

Nature Communications is currently edited by Nathalie Le Bot, Enda Bergin and Fiona Gillespie

More articles in Nature Communications from Nature
Bibliographic data for series maintained by Sonal Shukla () and Springer Nature Abstracting and Indexing ().