Nb1.60Ti0.32W0.08O5−δ as negative electrode active material for durable and fast-charging all-solid-state Li-ion batteries

Chanho Kim, Gyutae Nam, Yoojin Ahn, Xueyu Hu and Meilin Liu ()
Additional contact information
Chanho Kim: Georgia Institute of Technology
Gyutae Nam: Georgia Institute of Technology
Yoojin Ahn: Georgia Institute of Technology
Xueyu Hu: Georgia Institute of Technology
Meilin Liu: Georgia Institute of Technology

Nature Communications, 2024, vol. 15, issue 1, 1-10

Abstract: Abstract Li-based all-solid-state batteries (ASSBs) are considered feasible candidates for the development of the next generation of high-energy rechargeable batteries. However, ASSBs are detrimentally affected by a limited rate capability and inadequate performance at high currents. To circumvent these issues, here we propose the use of Nb1.60Ti0.32W0.08O5-δ (NTWO) as negative electrode active material. NTWO is capable of overcoming the limitation of lithium metal as the negative electrode, offering fast-charging capabilities and cycle stability. Physicochemical and electrochemical characterizations of NTWO in combination with the Li6PS5Cl (LPSCl) solid-state electrolyte demonstrate that the formation of LiWS2 at the electrode|electrolyte interphase is the main responsible for the improved battery performance. Indeed, when an NTWO-based negative electrode and LPSCl are coupled with a LiNbO3-coated LiNi0.8Mn0.1Co0.1O2-based positive electrode, the lab-scale cell is capable of maintaining 80% of discharge capacity retention after 5000 cycles at 45 mA cm−2 at 60 °C and 60 MPa.

Date: 2024
References: View references in EconPapers View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.nature.com/articles/s41467-024-52767-8 Abstract (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:nat:natcom:v:15:y:2024:i:1:d:10.1038_s41467-024-52767-8

Ordering information: This journal article can be ordered from
https://www.nature.com/ncomms/

DOI: 10.1038/s41467-024-52767-8

Access Statistics for this article

Nature Communications is currently edited by Nathalie Le Bot, Enda Bergin and Fiona Gillespie

More articles in Nature Communications from Nature
Bibliographic data for series maintained by Sonal Shukla () and Springer Nature Abstracting and Indexing ().