External acidity as performance descriptor in polyolefin cracking using zeolite-based materials

Sebastian Rejman, Zoé M. Reverdy, Zeynep Bör, Jaap N. Louwen, Carolin Rieg, Joren M. Dorresteijn, Jan-Kees Waal, Eelco T. C. Vogt, Ina Vollmer () and Bert M. Weckhuysen ()
Additional contact information
Sebastian Rejman: Utrecht University
Zoé M. Reverdy: Utrecht University
Zeynep Bör: Utrecht University
Jaap N. Louwen: Utrecht University
Carolin Rieg: Utrecht University
Joren M. Dorresteijn: Utrecht University
Jan-Kees Waal: TNO
Eelco T. C. Vogt: Utrecht University
Ina Vollmer: Utrecht University
Bert M. Weckhuysen: Utrecht University

Nature Communications, 2025, vol. 16, issue 1, 1-12

Abstract: Abstract Thermal pyrolysis is gaining industrial adoption to convert large volumes of plastic waste into hydrocarbon feedstock. However, it suffers from a high reaction temperature and relatively low selectivity. Utilizing a catalyst in the process, moving from thermal pyrolysis to catalytic cracking could help overcome both challenges. In order to develop efficient catalyst materials for this process, understanding structure-composition-performance relationships is critical. In this work, we show that in contrast to cracking of small molecules, plastic cracking activity using ultrastable zeolite Y materials does not depend on the bulk Brønsted acid site content, but rather on the concentration of acid sites located on the outer surface and in mesopores. This external acidity, however, fails to capture all the observed performance trends. Detailed kinetic experiments reveal that the scaling of the reaction rate with the catalyst loading differs drastically between highly similar catalyst materials. More specifically, doubling the catalyst loading leads to doubling of the reaction rate for one material, while for another it leads to more than fivefold increase. When very bulky reactants, such as polyolefins, are converted over microporous catalysts, structure-composition-performance relationships established for smaller molecules need to be revisited.

Date: 2025
References: Add references at CitEc
Citations:

Downloads: (external link)
https://www.nature.com/articles/s41467-025-57158-1 Abstract (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:nat:natcom:v:16:y:2025:i:1:d:10.1038_s41467-025-57158-1

Ordering information: This journal article can be ordered from
https://www.nature.com/ncomms/

DOI: 10.1038/s41467-025-57158-1

Access Statistics for this article

Nature Communications is currently edited by Nathalie Le Bot, Enda Bergin and Fiona Gillespie

More articles in Nature Communications from Nature
Bibliographic data for series maintained by Sonal Shukla () and Springer Nature Abstracting and Indexing ().