High electron mobility in thin films formed via supersonic impact deposition of nanocrystals synthesized in nonthermal plasmas

Elijah Thimsen (), Melissa Johnson, Xin Zhang, Andrew J. Wagner, K. Andre Mkhoyan, Uwe R. Kortshagen and Eray S. Aydil
Additional contact information
Elijah Thimsen: Environmental and Chemical Engineering, Washington University
Melissa Johnson: University of Minnesota
Xin Zhang: University of Minnesota
Andrew J. Wagner: University of Minnesota
K. Andre Mkhoyan: University of Minnesota
Uwe R. Kortshagen: University of Minnesota
Eray S. Aydil: University of Minnesota

Nature Communications, 2014, vol. 5, issue 1, 1-9

Abstract: Abstract Thin films comprising semiconductor nanocrystals are emerging for applications in electronic and optoelectronic devices including light emitting diodes and solar cells. Achieving high charge carrier mobility in these films requires the identification and elimination of electronic traps on the nanocrystal surfaces. Herein, we show that in films comprising ZnO nanocrystals, an electron acceptor trap related to the presence of OH on the surface limits the conductivity. ZnO nanocrystal films were synthesized using a nonthermal plasma from diethyl zinc and oxygen and deposited by inertial impaction onto a variety of substrates. Surprisingly, coating the ZnO nanocrystals with a few nanometres of Al2O3 using atomic layer deposition decreased the film resistivity by seven orders of magnitude to values as low as 0.12 Ω cm. Electron mobility as high as 3 cm2 V−1 s−1 was observed in films comprising annealed ZnO nanocrystals coated with Al2O3.

Date: 2014
References: Add references at CitEc
Citations:

Downloads: (external link)
https://www.nature.com/articles/ncomms6822 Abstract (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:nat:natcom:v:5:y:2014:i:1:d:10.1038_ncomms6822

Ordering information: This journal article can be ordered from
https://www.nature.com/ncomms/

DOI: 10.1038/ncomms6822

Access Statistics for this article

Nature Communications is currently edited by Nathalie Le Bot, Enda Bergin and Fiona Gillespie

More articles in Nature Communications from Nature
Bibliographic data for series maintained by Sonal Shukla () and Springer Nature Abstracting and Indexing ().