The effect of aging on the fracture resistance of different types of screw-cement-retained implant-supported zirconia-based restorations

Safoora Sahebi, Rashin Giti and Arian Sherafati

PLOS ONE, 2022, vol. 17, issue 6, 1-16

Abstract: Structural durability of screw-cement-retained implant-supported zirconia-based restorations is an important factor in choosing the best type of restoration for clinical use. This study aimed to evaluate the effects of thermocycling on the fracture resistance of different types of screw-cement-retained implant-supported zirconia-based restoration. Two experimental groups (monolithic zirconia and porcelain-veneered zirconia) and a control group of porcelain-fused-to-metal restorations were fabricated via CAD-CAM (n = 14 per group). Half of the specimens of each group (n = 7) were subjected to 10000 thermal cycles. The compressive force was applied and the force leading to fracture was measured by using a Universal Testing Machine. The fractured modes were classified under a scanning electron microscope. The data were analyzed through two-way ANOVA, one-way ANOVA, and independent samples t-test (α = 0.05). Among the non-thermocycled subgroups, the monolithic zirconia specimens were significantly more fracture-resistant than the porcelain-veneered zirconia and porcelain-fused-to-metal groups (P 0.05). Thermocycling decreased the fracture resistance of all groups; however, the difference was not statistically significant (P

Date: 2022
References: View complete reference list from CitEc
Citations:

Downloads: (external link)
https://journals.plos.org/plosone/article?id=10.1371/journal.pone.0270527 (text/html)
https://journals.plos.org/plosone/article/file?id= ... 70527&type=printable (application/pdf)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:plo:pone00:0270527

DOI: 10.1371/journal.pone.0270527

Access Statistics for this article

More articles in PLOS ONE from Public Library of Science
Bibliographic data for series maintained by plosone ().

 
Page updated 2025-05-31
Handle: RePEc:plo:pone00:0270527