Synergistic effect of chromium on the mechanical properties and microstructures of spheroidal graphite cast iron

Constantin Tshakatumba, Moramess Ngoy Moise Raphael, Héritier Tshipeshi Makina, Kaki Jospin Kiswakala Katwebe, Dieudonné Kyungu Mutumba and Guy Nkulu Wa Ngoie
Additional contact information
Constantin Tshakatumba: Metallography and Materials, Metallurgy, Polytechnics, University of Lubumbashi, DRC
Moramess Ngoy Moise Raphael: Metallography and Materials, Metallurgy, Polytechnics, University of Lubumbashi, DRC
Héritier Tshipeshi Makina: Metallography and Materials, Metallurgy, Polytechnics, University of Lubumbashi, DRC
Kaki Jospin Kiswakala Katwebe: Metallography and Materials, Metallurgy, Polytechnics, University of Lubumbashi, DRC
Dieudonné Kyungu Mutumba: Central Panda Workshops (ACP/Gecamines), Likasi, DRC
Guy Nkulu Wa Ngoie: Metallography and Materials, Metallurgy, Polytechnics, University of Lubumbashi, DRC

Technium, 2021, vol. 3, issue 3, 41-52

Abstract: The fragmentation equipment used in ore’s preparation operations is internally lined with armor whose characteristics require better wear resistance and resilience. The aim of this study was to develop a new generation of high-performance 4% Cr spheroidal graphite (GS) cast iron materials for the manufacture of self-growing shredder lift bars. This typeface was designed in the optic to replace the commonly used white cast iron. The results were used to assess the effect of chromium on the microstructure of the cast iron as well as on its mechanical behavior. It is noted that the presence of chromium leads to the appearance of eutectic carbides and out-of-balance dies. Two types of chromium carbide (Fe,Cr)7C3 and (Fe,Cr)3C precipitate into the matrix and effectively contribute to the improvement of mechanical performances of this material.The quench and tempering heat treatments applied to these materialsled to the following optimum values: impact resistance of 4.8 J/cm2 for the GS 4Cr nuance, 5 J/cm2 for the GS nuance and 0.9 J/cm2 for the 9 cast iron nuance; hardness values of 691, 511 and 509 HV30 were measured respectively for GS 4Cr cast iron, GS cast iron and 9 cast iron treated. The optimal lifetime of each material was estimated at approximately 285 days for treated GS cast iron, 585 days for GS 4Cr cast iron treated and 242 days for normalized cast iron 9.

Date: 2021
References: Add references at CitEc
Citations:

Downloads: (external link)
https://techniumscience.com/index.php/technium/article/view/3042 (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:tec:techni:ojs:3042

Access Statistics for this article

Technium is currently edited by Scurtu Ionut Cristian

More articles in Technium from Technium Science
Bibliographic data for series maintained by Ana Maria Golita ().