FRETTING WEAR BEHAVIOR OF TIN PLATED CONTACTS: INFLUENCE ON CONTACT RESISTANCE

Young Woo Park, T. S. N. Sankara Narayanan and Kang Yong Lee ()
Additional contact information
Young Woo Park: Stress Analysis and Failure Design Laboratory, School of Mechanical Engineering, Yonsei University, 134, Sinchon-dong, Seodaemum-gu, Seoul 120-749, South Korea
T. S. N. Sankara Narayanan: Stress Analysis and Failure Design Laboratory, School of Mechanical Engineering, Yonsei University, 134, Sinchon-dong, Seodaemum-gu, Seoul 120-749, South Korea
Kang Yong Lee: Stress Analysis and Failure Design Laboratory, School of Mechanical Engineering, Yonsei University, 134, Sinchon-dong, Seodaemum-gu, Seoul 120-749, South Korea

Surface Review and Letters (SRL), 2006, vol. 13, issue 05, 635-644

Abstract: The fretting wear behavior of tin plated copper alloy contacts and its influence on the contact resistance are addressed in this paper. Based on the change in the area of contact zone as well as the wear depth as a function of fretting cycles, a model was proposed to explain the observed low and stable contact resistance. The extent of wear of tin coating and the formation of wear debris as a function of fretting cycles were assessed by scanning electron microscopy (SEM). Energy dispersive X-ray line scanning (EDX), X-ray mapping, and EDX spot analysis were employed to characterize the nature of changes that occur at the contact zone. The study reveals that the fretted area increases linearly up to 8000 cycles due to the continuous removal of the tin coating and attains saturation when the fretting path length reaches a maximum. The observed low and stable contact resistance observed up to 8000 cycles is due to the common area of contact which provides an electrically conducting area. Surface analysis by SEM, EDX, and X-ray elemental mapping elucidate the nature of changes that occurred at the contact zone. Based on the change in contact resistance as a function of fretting cycles, the fretting wear and fretting corrosion dominant regimes are proposed. The interdependence of extent of wear and oxidation increases the complexity of the fretting corrosion behavior of tin plated contacts.

Keywords: Fretting wear; tin plated contact; contact resistance; surface analysis (search for similar items in EconPapers)
Date: 2006
References: View complete reference list from CitEc
Citations:

Downloads: (external link)
http://www.worldscientific.com/doi/abs/10.1142/S0218625X06008591
Access to full text is restricted to subscribers

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:wsi:srlxxx:v:13:y:2006:i:05:n:s0218625x06008591

Ordering information: This journal article can be ordered from

DOI: 10.1142/S0218625X06008591

Access Statistics for this article

Surface Review and Letters (SRL) is currently edited by S Y Tong

More articles in Surface Review and Letters (SRL) from World Scientific Publishing Co. Pte. Ltd.
Bibliographic data for series maintained by Tai Tone Lim ().