REUSABILITY OF SERS-ACTIVE SURFACES BASED ON GOLD-DECORATED HEXAGONAL ZnO NANOROD USED ZINC SHEET AS TEMPLATE

W. Koetniyom, P. Somboonsaksri, J. Prasobchokchaikun, S. Kalasung, N. Nuntawong, V. Patthanasettakul, M. Horprathum, S. Limwichean and P. Eiamchai
Additional contact information
W. Koetniyom: Department of Industrial Physics and Medical Instrumentation, Faculty of Applied Science, King Mongkut’s University of Technology, North Bangkok, Bangkok, Thailand†Lasers and Optics Research Center (LANDOS), King Mongkut’s University of Technology, North Bangkok, Bangkok, Thailand
P. Somboonsaksri: Department of Industrial Physics and Medical Instrumentation, Faculty of Applied Science, King Mongkut’s University of Technology, North Bangkok, Bangkok, Thailand
J. Prasobchokchaikun: Department of Industrial Physics and Medical Instrumentation, Faculty of Applied Science, King Mongkut’s University of Technology, North Bangkok, Bangkok, Thailand
S. Kalasung: #x2021;Optical Thin-Film Technology Laboratory, National Electronics and Computer Technology Center, National Science and Technology Development Agency, Pathum Thani, Thailand
N. Nuntawong: #x2021;Optical Thin-Film Technology Laboratory, National Electronics and Computer Technology Center, National Science and Technology Development Agency, Pathum Thani, Thailand
V. Patthanasettakul: #x2021;Optical Thin-Film Technology Laboratory, National Electronics and Computer Technology Center, National Science and Technology Development Agency, Pathum Thani, Thailand
M. Horprathum: #x2021;Optical Thin-Film Technology Laboratory, National Electronics and Computer Technology Center, National Science and Technology Development Agency, Pathum Thani, Thailand
S. Limwichean: #x2021;Optical Thin-Film Technology Laboratory, National Electronics and Computer Technology Center, National Science and Technology Development Agency, Pathum Thani, Thailand
P. Eiamchai: #x2021;Optical Thin-Film Technology Laboratory, National Electronics and Computer Technology Center, National Science and Technology Development Agency, Pathum Thani, Thailand

Surface Review and Letters (SRL), 2018, vol. 25, issue Supp01, 1-6

Abstract: In this study, surface-enhanced Raman spectroscopic (SERS) substrates with reusability were carefully fabricated and investigated. Based on a simple and cost-effective hydrothermal process, zinc sheets were used as a base for growing zinc oxide nanorods (ZnO NRs) with hexagonal structures as templates for the SERS substrates. In the experimentation, the authors explored a variation of the physical NR structures based on precursors of zinc nitrate (Zn(NO3)2): hexamethylenetetramine (HMTA) at 1:1 ratio, in aqueous solution with DI water at a concentration of 2.5–20mM. The prepared zinc oxide templates were finally decorated with gold nanoparticles (Au NPs) with the sputtering deposition for 90s in order to promote the SERS-active surface. From physical observations, the scanning electron microscopic (SEM) results showed that the ZnO NRs exhibited an increase in size from 56.4nm to 244.06nm as the solution concentration was increased. Further investigations also demonstrated that the Au-decorated SERS-active samples had the gold nanoparticles covering the top of the ZnO NRs. The prepared SERS substrates were finally measured for the Raman enhancement with methylene blue (MB) as the test molecules. The results showed that the SERS substrates could detect the Raman peaks of the MB at the limit of detection of 1×10−6M. In addition, the SERS substrates were tested for reusability with the UV exposure, up to at least nine cycles. This work therefore reported the progress of the fabrications of the SERS-active materials with the reusable potentials in several SERS applications.

Keywords: Surface-enhanced Raman spectroscopic; reusability; zinc oxide; hydrothermal; hexagonal structure; sputtering (search for similar items in EconPapers)
Date: 2018
References: Add references at CitEc
Citations:

Downloads: (external link)
http://www.worldscientific.com/doi/abs/10.1142/S0218625X18400048
Access to full text is restricted to subscribers

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:wsi:srlxxx:v:25:y:2018:i:supp01:n:s0218625x18400048

Ordering information: This journal article can be ordered from

DOI: 10.1142/S0218625X18400048

Access Statistics for this article

Surface Review and Letters (SRL) is currently edited by S Y Tong

More articles in Surface Review and Letters (SRL) from World Scientific Publishing Co. Pte. Ltd.
Bibliographic data for series maintained by Tai Tone Lim ().