EFFECT OF COATING TIME ON ELECTROCHEMICAL DEPOSITION OF MOLYBDENUM OXIDES THIN FILM ON THE SURFACE OF ANODIZED ALUMINUM PLATE FOR ULTRACAPACITOR ELECTRODE MATERIAL

Wandee Thamjaree () and Wim Nhuapeng ()
Additional contact information
Wandee Thamjaree: Center of Excellence in Materials Science and Technology, Faculty of Science, Chiang Mai University, Chiang Mai, 50200, Thailand
Wim Nhuapeng: Center of Excellence in Materials Science and Technology, Faculty of Science, Chiang Mai University, Chiang Mai, 50200, Thailand

Surface Review and Letters (SRL), 2018, vol. 25, issue Supp01, 1-5

Abstract: In this work, effect of coating time on the structural, compositional and morphological properties of MoO3-coated Al2O3 plate for application as an electrode material for ultracapacitor was investigated. The 1cm × 1cm aluminum plate was anodized by an electrochemical plating technique at 12V for 20 and 30min, respectively. MoO3 film was then coated on anodized aluminum plate over a range of coating time (2–10min, in intervals of 4min) at an applied voltage of 6V with constant electric current of 1A. X-ray photoelectron spectroscopy (XPS), energy dispersive X-ray spectroscopy (EDX) and scanning electron microscopy (SEM) were employed in the characterization of the MoO3/Al2O3 plate obtained. The SEM results obtained indicated that the coating time significantly affected the roughness and the surface area of the samples. The EDX analysis revealed the chemical composition element of Mo, O and Al and the result from XPS confirmed the existence of MoO3.

Keywords: Molybdenum oxide; electrochemical plating; anodized aluminum; coating time (search for similar items in EconPapers)
Date: 2018
References: View complete reference list from CitEc
Citations:

Downloads: (external link)
http://www.worldscientific.com/doi/abs/10.1142/S0218625X18400073
Access to full text is restricted to subscribers

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:wsi:srlxxx:v:25:y:2018:i:supp01:n:s0218625x18400073

Ordering information: This journal article can be ordered from

DOI: 10.1142/S0218625X18400073

Access Statistics for this article

Surface Review and Letters (SRL) is currently edited by S Y Tong

More articles in Surface Review and Letters (SRL) from World Scientific Publishing Co. Pte. Ltd.
Bibliographic data for series maintained by Tai Tone Lim ().

 
Page updated 2025-03-20
Handle: RePEc:wsi:srlxxx:v:25:y:2018:i:supp01:n:s0218625x18400073