A NOVEL STUDY ON SURFACE MODIFICATION OF PALMYRA FIBERS FOR ENHANCING MECHANICAL AND THERMAL PROPERTIES

T. Raghavendra () and K. Panneerselvam
Additional contact information
T. Raghavendra: Department of Production Engineering, National Institute of Technology, Tiruchirappalli – 620015, Tamil Nadu, India
K. Panneerselvam: Department of Production Engineering, National Institute of Technology, Tiruchirappalli – 620015, Tamil Nadu, India

Surface Review and Letters (SRL), 2020, vol. 27, issue 02, 1-11

Abstract: Natural fiber reinforcing in engineering thermoplastics (Nylon melting point around 230∘C) is challenging, due to the lower degradation temperature (∼180∘C) of lignocellulosic fibers. Further, increasing temperature (beyond 200∘C) results in weakening of its mechanical properties. In this investigation, camphor soot reinforced palmyra fibers (CSRPF) are manufactured by osmosis with the help of design of experiments (DOE) and are examined for different time (4, 8 and 12h), temperature (30∘C, 40∘C and 50∘C) and camphor soot concentrations (0.5, 1.0 and 1.5wt.%) using L9 orthogonal array. The osmosis rate of modified fibers was calculated and tested for their tensile strength as the osmosis rate and tensile strength are the main objective functions. Based on DOE and taguchi-ANOVA analysis, optimal parameters were obtained through main effect plots and Anova results. Further, an optimal combination of parameters for CSRPF was characterized for thermogravimetric analysis (TGA), Fourier transform infrared radiation (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersion spectroscopy (EDS) to inspect and compare it with neat palmyra fibers. There was considerable improvement in the CSRPF tensile strength about 84Mpa with respect to neat palmyra fibers which is 58MPa. TGA reveals the degradation temperature of neat palmyra fiber is about 225∘C and it is enhanced in case of CSRPF about 265∘C which accounts for 15% enhanced thermal stability. The crystallinity index (CI) of CSRPF was reduced marginally compared to the neat palmyra fibers. FTIR analysis showed the peak drift marginally to the left in CSRPF due to the coating of camphor soot particles. The microstructure of both neat and CSRPF are examined using SEM and EDS which shows that 93.71% carbon was present in the cross section of CSRPF compared to the neat palmyra fiber (62.58%).

Keywords: Osmosis; camphor soot; palmyra fibers; thermal stability; scanning electron microscope (search for similar items in EconPapers)
Date: 2020
References: Add references at CitEc
Citations:

Downloads: (external link)
http://www.worldscientific.com/doi/abs/10.1142/S0218625X1950104X
Access to full text is restricted to subscribers

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:wsi:srlxxx:v:27:y:2020:i:02:n:s0218625x1950104x

Ordering information: This journal article can be ordered from

DOI: 10.1142/S0218625X1950104X

Access Statistics for this article

Surface Review and Letters (SRL) is currently edited by S Y Tong

More articles in Surface Review and Letters (SRL) from World Scientific Publishing Co. Pte. Ltd.
Bibliographic data for series maintained by Tai Tone Lim ().

 
Page updated 2025-03-20
Handle: RePEc:wsi:srlxxx:v:27:y:2020:i:02:n:s0218625x1950104x