EFFECT OF LOADING ON DEGRADATION OF TAPER ROLLER BEARING USING VIBRATION SIGNAL

Manpreet Singh, Rajeev Kumar and Sumit Shoor
Additional contact information
Manpreet Singh: School of Mechanical Engineering, Lovely Professional University, Phagwara, Punjab, India
Rajeev Kumar: School of Mechanical Engineering, Lovely Professional University, Phagwara, Punjab, India
Sumit Shoor: School of Mechanical Engineering, Lovely Professional University, Phagwara, Punjab, India

Surface Review and Letters (SRL), 2023, vol. 30, issue 06, 1-11

Abstract: Studies reveal that the most prominent cause of bearing failure is a crack on any of its mating surfaces. When the crack is initiated, the bearing can still be used for some duration, but this is majorly depending upon the loading conditions. This work primarily focuses on the effects of different levels of static loading on the crack propagation after crack initiation. To analyze the effect of static loading, an axial groove defect was seeded on the outer race of a taper roller bearing randomly and bearing run continuously under five different static loading conditions. Initially, the bearing was made to run under loading conditions to initiate the crack naturally but the crack was not initiated even after 800 h of running. Therefore, crack was initiated artificially for the purpose of studying crack propagation. It was observed from the experimentation that in the case of maximum static load of 20 kg, the crack propagates rapidly in terms of area after 109 h of continuous running, whereas in the case of no load, it started propagating quickly after 267.5 h of running. Statistical analysis was also carried out for the recorded signals at different intervals of times, and it was observed that the Shannon entropy value was showing a sudden rise with the edge breakage (visually verified) while the crack was propagating. However, in the statistical analysis, none of the parameters showed a correlation with crack propagation. To develop the correlation of crack propagation, Shannon entropy of high, medium and low frequency bands of continuous wavelet-based (CWT) was carried out using different wavelets. Shannon entropy for high frequency band of CWT using Daubechies 10 as mother wavelet has responded well to the crack propagation as the value showed a sudden rise and an overall increase for edge breakage and crack propagation, respectively. A high frequency band of CWT using Daubechies 10 was found suitable for detecting edge breakage and crack growth at the same time because of its capability to respond to transient characteristics for a large duration of time.

Keywords: Vibration analysis; condition monitoring; wavelet; crack propagation; effect of loading (search for similar items in EconPapers)
Date: 2023
References: Add references at CitEc
Citations:

Downloads: (external link)
http://www.worldscientific.com/doi/abs/10.1142/S0218625X2350035X
Access to full text is restricted to subscribers

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:wsi:srlxxx:v:30:y:2023:i:06:n:s0218625x2350035x

Ordering information: This journal article can be ordered from

DOI: 10.1142/S0218625X2350035X

Access Statistics for this article

Surface Review and Letters (SRL) is currently edited by S Y Tong

More articles in Surface Review and Letters (SRL) from World Scientific Publishing Co. Pte. Ltd.
Bibliographic data for series maintained by Tai Tone Lim ().

 
Page updated 2025-03-20
Handle: RePEc:wsi:srlxxx:v:30:y:2023:i:06:n:s0218625x2350035x