SYNTHESIS OF FUNCTIONALIZED GRAPHENE NANOPLATELETS THROUGH OXIDATIVE CHLOROPHOSPHORYLATION: TECHNICAL NOTE

Solmaz Aliyeva, Rasim Alosmanov and Irada Buniyatzadeh
Additional contact information
Solmaz Aliyeva: Scientific-Research Institute “Geotechnological Problems of Oil, Gas and Chemistry†, Azerbaijan State Oil and Industry University, D. Aliyeva 227, Baku AZ1010, Azerbaijan
Rasim Alosmanov: ��Baku State University, Z. Khalilov 23, Baku AZ1148, Azerbaijan, Department of Chemistry of High Molecular Weight Compounds, Azerbaijan
Irada Buniyatzadeh: ��Baku State University, Z. Khalilov 23, Baku AZ1148, Azerbaijan, Department of Chemistry of High Molecular Weight Compounds, Azerbaijan

Surface Review and Letters (SRL), 2023, vol. 30, issue 07, 1-12

Abstract: This paper is devoted to the investigation of functionalized graphene nanoplatelets (FGNPs) samples. Synthesis of FGNPs was carried out through oxidative chlorophosphorylation (OxCh) reaction, i.e. reaction of graphite with PCl3 in the presence of oxygen under different conditions. For this, the reaction of graphite with PCl3 in the presence of oxygen was carried out separately both at a temperature of 65°C and at room temperature in a CCl4 medium and at a temperature of 65°C in a CCl4 medium. The FGNPs samples obtained by this method were named FGNPs1, FGNPs2, and FGNPs3, respectively. FGNPs1, FGNPs2, and FGNPs3 were investigated using Fourier Transform Infrared (FTIR) and ultraviolet–visible (UV–Visible) spectroscopy, scanning electron microscopy (SEM), and X-ray diffraction (XRD) analysis methods. The results of FTIR spectroscopy showed that all FGNPs samples contain phosphonate groups. Based on the UV–Vis spectroscopy, the optical band gap of the samples was calculated and compared with pristine graphite. It has been established that the width of the optical bands of FGNPs1 (1.17eV), FGNPs2 (1.22eV), and FGNPs3 (1.24eV) is wider than that of the pristine graphite (1.04eV). Based on the XRD analysis, it was determined that the functionalization causes a change in the crystal lattice parameters of graphite. Based on the XRD analysis, it was determined that the functionalization causes a change in the crystal lattice parameters of graphite and FGNPs samples (number of graphene layers: FGNPs1=∼45; FGNPs2=∼42; FGNPs3=∼37) to consist of fewer graphene layers than graphite (∼120).

Keywords: Graphene nanoplatelets; graphite; ultraviolet-visible spectroscopy; infrared spectroscopy; X-ray diffraction (search for similar items in EconPapers)
Date: 2023
References: Add references at CitEc
Citations:

Downloads: (external link)
http://www.worldscientific.com/doi/abs/10.1142/S0218625X23500464
Access to full text is restricted to subscribers

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:wsi:srlxxx:v:30:y:2023:i:07:n:s0218625x23500464

Ordering information: This journal article can be ordered from

DOI: 10.1142/S0218625X23500464

Access Statistics for this article

Surface Review and Letters (SRL) is currently edited by S Y Tong

More articles in Surface Review and Letters (SRL) from World Scientific Publishing Co. Pte. Ltd.
Bibliographic data for series maintained by Tai Tone Lim ().