THERMAL SHOCK BEHAVIOR OF LANTHANUM ZIRCONATE-BASED THERMAL BARRIER COATINGS

KARABAÅž Muhammet () and Emre Bal
Additional contact information
KARABAŞ Muhammet: Lüleburgaz Faculty of Aeronautics and Astronautics, Kırklareli University, Turkey
Emre Bal: ��Faculty of Engineering, Akdeniz University, 07070 Antalya, Turkey

Surface Review and Letters (SRL), 2024, vol. 31, issue 04, 1-9

Abstract: In this study, La2Zr2O7, Yb2O3 and Gd2O3-doped La1.4(Gd, Yb)0.6Zr2O7 thermal barrier coatings have been manufactured from the crystalline and amorphous feedstock by plasma spraying. The thickness of the bond coat is 100±25 μm and the thickness of the top coat is 250±25 μm. Thermal shock tests were carried out in furnace temperature of 1200∘C. The thermal shock tests indicate that lifetime of the La1.4Gd0.6Zr2O7 coating has 55 cycles which is the highest thermal shock lifetime compared to other coatings in this study. The type of feedstock, amorphous or crystalline, strongly affects the thermal shock lifetime of La2Zr2O7 coatings. Coating damage after thermal shock tests was investigated using scanning electron microscope to observe the microstructure and X-ray diffraction techniques to analyze the phase composition. The failure of coatings is mainly in consequence of the accumulation of stress between bond coat–ceramic coat interface due to thermal expansion coefficient differences and thermally grown oxide layer formation during thermal shock cycling tests.

Keywords: Thermal barrier coating; thermal shock resistance; failure analysis; microstructure (search for similar items in EconPapers)
Date: 2024
References: Add references at CitEc
Citations:

Downloads: (external link)
http://www.worldscientific.com/doi/abs/10.1142/S0218625X24500276
Access to full text is restricted to subscribers

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:wsi:srlxxx:v:31:y:2024:i:04:n:s0218625x24500276

Ordering information: This journal article can be ordered from

DOI: 10.1142/S0218625X24500276

Access Statistics for this article

Surface Review and Letters (SRL) is currently edited by S Y Tong

More articles in Surface Review and Letters (SRL) from World Scientific Publishing Co. Pte. Ltd.
Bibliographic data for series maintained by Tai Tone Lim ().