Cycle aging of commercial NMC/graphite pouch cells at different temperatures

K. Jalkanen, J. Karppinen, L. Skogström, T. Laurila, M. Nisula and K. Vuorilehto

Applied Energy, 2015, vol. 154, issue C, 160-172

Abstract: Cycle aging of commercial 40Ah pouch-type lithium-ion cells with NMC/graphite chemistry was studied at different cycling temperatures (room temperature, +45°C, and +45°C charge/+65°C discharge). Aging was observed as capacity fade and resistance increase, and the aging mechanisms were characterized by electrochemical impedance spectroscopy and post-mortem analysis, where visual inspection and thickness measurements were employed together with X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), and inductively coupled plasma optical emission spectroscopy (ICP-OES) analyses. It was observed that elevated temperatures resulted in accelerated capacity fade, especially for the +45°C/+65°C condition. SEI-layer growth and lithium plating, discovered in cell disassembly, were attributed to be the main mechanisms responsible for capacity loss. In addition to the capacity fade, resistance increase was observed both in ohmic and polarization resistances. The ohmic resistance growth was attributed to lack of electrolyte and increased separator resistance. Polarization resistance evolution during cycling was similar at room temperature and at +45°C, but different at the +45°C/+65°C condition. It was concluded that post-mortem analysis is essential for attributing the cycle testing and impedance spectroscopy results to different components and processes inside the cell. For example, the lithium plating phenomenon could not have been predicted or discovered without disassembling the cells.

Keywords: Lithium-ion battery lifetime; Commercial pouch cell; Cycle aging; Aging mechanisms; Post-mortem analysis; Lithium plating (search for similar items in EconPapers)
Date: 2015
References: View references in EconPapers View complete reference list from CitEc
Citations: View citations in EconPapers (20)

Downloads: (external link)
http://www.sciencedirect.com/science/article/pii/S0306261915005735
Full text for ScienceDirect subscribers only

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:eee:appene:v:154:y:2015:i:c:p:160-172

Ordering information: This journal article can be ordered from
http://www.elsevier.com/wps/find/journaldescription.cws_home/405891/bibliographic
http://www.elsevier. ... 405891/bibliographic

DOI: 10.1016/j.apenergy.2015.04.110

Access Statistics for this article

Applied Energy is currently edited by J. Yan

More articles in Applied Energy from Elsevier
Bibliographic data for series maintained by Catherine Liu ().