Bond Strength and Fracture Toughness of Alkali Activated Self-Compacting Concrete Incorporating Metakaolin or Nanosilica

Radhwan Alzeebaree
Additional contact information
Radhwan Alzeebaree: Department of Highways and Bridges, Duhok Polytechnic University, Duhok 42001, Iraq

Sustainability, 2022, vol. 14, issue 11, 1-32

Abstract: This study aims to evaluate the effect of nanosilica (NS) and metakaolin (MK) as binder replacement materials on the fresh and hardened characteristics of slag (GGBS)-based alkali-activated self-compacting concretes (A-ASCC). Therefore, nine A-ASCC mixes, with and without metakaolin, were prepared, as well as mixes with and without NS incorporation. In the production of A-ASCC mixes, GGBS was used as a binder material. The fresh properties of A-ASCC were determined using the L-box, V-funnel, T50 value, and slump flow tests, while the hardened properties were examined using compressive strength, bonding strength (pullout test), fracture toughness, and flexural tensile strength tests. A relationship analysis was also conducted on the A-ASCC experimental data. The experimental results showed that NS and MK had a negative effect on the fresh properties of GGBS-based A-ASCC mixtures, whereas metakaolin had a greater influence. The addition of 1% and 2% NS, on the other hand, improved the mechanical performance of the A-ASCC specimens significantly. The use of more than 2% NS had a harmful effect on the mechanical properties of A-ASCC. A 5% replacement ratio of metakaolin improved the mechanical properties of A-ASCC. The use of metakaolin at ratios of more than 5% had a negative effect on the properties of A-ASCC.

Keywords: bond strength; fracture toughness; fresh properties; alkali-activated self-compacting concrete; nanosilica; and metakaolin (search for similar items in EconPapers)
JEL-codes: O13 Q Q0 Q2 Q3 Q5 Q56 (search for similar items in EconPapers)
Date: 2022
References: View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.mdpi.com/2071-1050/14/11/6798/pdf (application/pdf)
https://www.mdpi.com/2071-1050/14/11/6798/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jsusta:v:14:y:2022:i:11:p:6798-:d:830128

Access Statistics for this article

Sustainability is currently edited by Ms. Alexandra Wu

More articles in Sustainability from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().