Technological Evaluation of Algae-Based Fillers for Polymer 3D Printing

Maximilian Fiedler (), Oliver Schoemig, Fabian Fischer and Klaus Droeder
Additional contact information
Maximilian Fiedler: Volkswagen AG, Berliner Ring 2, 38436 Wolfsburg, Germany
Oliver Schoemig: Institute of Machine Tools and Production Technology, Technical University of Braunschweig, Langer Kamp 19b, 38106 Braunschweig, Germany
Fabian Fischer: Volkswagen AG, Berliner Ring 2, 38436 Wolfsburg, Germany
Klaus Droeder: Institute of Machine Tools and Production Technology, Technical University of Braunschweig, Langer Kamp 19b, 38106 Braunschweig, Germany

Sustainability, 2023, vol. 15, issue 5, 1-13

Abstract: One approach to reducing the environmental footprint of conventional polymers is to compound them with bio-based fillers. Plant-based materials have already been successfully used as polymer fillers. In this context, algae-based fillers received minor attention. Due to their unique growth efficiency and ability to capture large amounts of CO 2 , the use of algae-based fillers could have economic and ecologic advantages. In this work, a possible use of algae as a sustainable filler for filament materials was technologically evaluated. In practical investigations, conventional polyethylene-terephthalate-glycol (PETG) was mixed with the microalgae spirulina platensis and chlorella vulgaris and extruded to 3D printing filaments. Based on printed test specimens and material samples, the printability, mechanical, and thermal properties of the composite were determined. Filaments with a homogeneous distribution of algae particles and stable diameters up to a filler content of 30 wt.% could be produced. All filaments had good printability and adequate moisture sensitivity for higher algae contents. For 30 wt.% the tensile strength of the produced filaments decreases from 54 MPa to 24 MPa, the flexural strength decreases from 87 MPa to 69 MPa, and the material operating temperature decreases slightly from 70 °C to 66 °C. The addition of smaller amounts of algae results in minor changes regarding the overall performance. The properties of the material were comparable to those of other natural fillers such as wood, bamboo or cork. The main objective of adding bio-based materials to polymeric matrices can be achieved. Our results suggest that algae-based filaments can be produced as a more sustainable and low-cost material.

Keywords: additive manufacturing; fused deposition modeling; sustainable materials; algae; bio-based (search for similar items in EconPapers)
JEL-codes: O13 Q Q0 Q2 Q3 Q5 Q56 (search for similar items in EconPapers)
Date: 2023
References: View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.mdpi.com/2071-1050/15/5/4039/pdf (application/pdf)
https://www.mdpi.com/2071-1050/15/5/4039/ (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:gam:jsusta:v:15:y:2023:i:5:p:4039-:d:1077437

Access Statistics for this article

Sustainability is currently edited by Ms. Alexandra Wu

More articles in Sustainability from MDPI
Bibliographic data for series maintained by MDPI Indexing Manager ().