Supramolecular nanocrystalline membranes with well-aligned subnanochannels for enhanced reverse osmosis desalination

Gang Lu (), Wentao Shang, Xinyao Ma, Hengyue Xu, Hubao A, Jiawei Sun, Xiaolu Li, Mingyi Jia, Shuang Lu, Jun Wu, Xi Chen, Shensheng Chen, Jun Fan () and Alicia Kyoungjin An ()
Additional contact information
Gang Lu: City University of Hong Kong
Wentao Shang: City University of Hong Kong
Xinyao Ma: City University of Hong Kong
Hengyue Xu: Tsinghua University
Hubao A: Wuhan University
Jiawei Sun: City University of Hong Kong
Xiaolu Li: City University of Hong Kong
Mingyi Jia: City University of Hong Kong
Shuang Lu: Nansha Drainage and Sewage Treatment Center
Jun Wu: Harbin Engineering University
Xi Chen: City University of Hong Kong
Shensheng Chen: The Hong Kong University of Science and Technology
Jun Fan: City University of Hong Kong
Alicia Kyoungjin An: City University of Hong Kong

Nature Communications, 2025, vol. 16, issue 1, 1-13

Abstract: Abstract Thin-film composite membranes are integral to the reverse osmosis (RO) process, effectively converting seawater and brackish water into potable water. While significant strides have been made in improving water permeability and salt rejection, there has been a corresponding lag in enhancing chlorine resistance and boron rejection. This study presents a suprasmolecular nanocrystalline membrane (SNM) with abundant subnanometer channels created through precisely assembled and well-oriented tetra-oligomer chains, enhanced by interfacial hydrogen bonding under nanoconfined space. The 6 nm-thick SNM exhibits highly aligned nanocrystalline domains and a Young’s modulus of 4 ± 0.5 GPa. Benefiting from its ultrathin thickness and well-oriented subnanoscale channels, the SNM functions effectively as a permeation and selective layer, achieving 99.6% NaCl rejection at 55 bar with a 3.5 wt% NaCl feed and delivering 2-4 times higher water permeance than commercial seawater RO membranes. Molecular dynamics simulations reveal that the abundant, well-aligned subnanochannels facilitate rapid water transport while raising the energy barrier for sodium ion transport. Furthermore, the SNM shows superior boron rejection (exceeding 92.5% at pH 7), remarkable chlorine resistance (200 ppm NaClO exposure for 300 hours), and sustained operational stability under extreme pH conditions (1 and 13) for over 168 hours. These findings establish that space-confined interfacial hydrogen bonding governs the precision self-assembly of robust subnanochannels, offering a new paradigm for high-resilience desalination membranes.

Date: 2025
References: View complete reference list from CitEc
Citations:

Downloads: (external link)
https://www.nature.com/articles/s41467-025-61352-6 Abstract (text/html)

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:nat:natcom:v:16:y:2025:i:1:d:10.1038_s41467-025-61352-6

Ordering information: This journal article can be ordered from
https://www.nature.com/ncomms/

DOI: 10.1038/s41467-025-61352-6

Access Statistics for this article

Nature Communications is currently edited by Nathalie Le Bot, Enda Bergin and Fiona Gillespie

More articles in Nature Communications from Nature
Bibliographic data for series maintained by Sonal Shukla () and Springer Nature Abstracting and Indexing ().