The permeability of geopolymer at down-hole stress conditions: Application for carbon dioxide sequestration wells

M.C.M. Nasvi, P.G. Ranjith and J. Sanjayan

Applied Energy, 2013, vol. 102, issue C, 1398 pages

Abstract: Emissions of greenhouse gases have been a major problem for the world for many decades, and the geo-sequestration of carbon dioxide (CO2) has been proposed as one of the best solutions for the reduction of anthropogenic greenhouse gas emissions. The injection well and the well cement play vital roles in the sustainability of a sequestration project, and CO2 leakage through the wellbore and well cement has been found to be the major threat to the success of sequestration projects. Therefore, the permeability of well cement should be low to avoid leakage in the wellbore. To date, ordinary Portland cement (OPC) based well cement has been used, and it has been found to be unstable in the CO2 environment as it provides pathways for CO2 leakage. One of the best replacements for OPC would be geopolymer cement as it possesses excellent strength, acid resistance and durability compared to OPC. Therefore, this paper addresses geopolymer as well cement in place of OPC and discusses its permeability. In the first phase of this work, previous studies relevant to the permeability of existing oil well cement and geopolymer cement were analysed. In the second phase, an experimental study was conducted to study the CO2 permeability of geopolymer under tri-axial conditions, using the high pressure tri-axial set-up available in the Monash University laboratory. Based on the experimental results, the apparent CO2 permeability of geopolymer is in the range of 2×10−21–6×10−20m2 and it is less than the CO2 permeability of typical oil well cement (10−20–10−11m2). This indicates that geopolymer is a good replacement for existing OPC-based cement as it has lower CO2 permeability. At a given confining pressure, the permeability of geopolymer reduces with the increase in injection pressure and this is attributed to Klinkenberg’s effect. When the confining pressure is increased from 10 to 25MPa, the permeability reduction is 60% at lower injection pressures (5MPa). The corresponding reduction is 35% at higher injection pressures (>10MPa) as the permeability value reaches its intrinsic permeability at higher injection pressures. In addition, CO2 permeability reduces with confining stress for all the injection pressures studied.

Keywords: Carbon dioxide; Geopolymer; Geo-sequestration; Permeability; Well cement (search for similar items in EconPapers)
Date: 2013
References: View complete reference list from CitEc
Citations: View citations in EconPapers (2)

Downloads: (external link)
http://www.sciencedirect.com/science/article/pii/S0306261912006447
Full text for ScienceDirect subscribers only

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:eee:appene:v:102:y:2013:i:c:p:1391-1398

Ordering information: This journal article can be ordered from
http://www.elsevier.com/wps/find/journaldescription.cws_home/405891/bibliographic
http://www.elsevier. ... 405891/bibliographic

DOI: 10.1016/j.apenergy.2012.09.004

Access Statistics for this article

Applied Energy is currently edited by J. Yan

More articles in Applied Energy from Elsevier
Bibliographic data for series maintained by Catherine Liu ().