Physical degradation of cathode catalyst layer: A major contributor to accelerated water flooding in long-term operation of DMFCs

Asad Mehmood, Myung-Gi An and Heung Yong Ha

Applied Energy, 2014, vol. 129, issue C, 346-353

Abstract: This study presents a comprehensive investigation on the water flooding of direct methanol fuel cells (DMFCs) during long-term testing with regard to the structural changes of the catalyst layer and gas diffusion layer (GDL) of the cathode. Two separate durability operations of DMFCs are conducted for 1000 and 1261h in order to determine the relative contributions of the cathode catalyst layer and the GDL to time-dependent water flooding during the aging process. The voltage decay rates caused by flooding and non-flooding degradation phenomena are calculated and compared. DMFCs undergo serious voltage decay due to water accumulation in the cathode, and the rate of flooding degradation multiplies approximately every 500h during the duration of testing. The cathode catalyst layer is found to be severely deformed due to surface wrinkling and cracking during the aging of the membrane electrode assembly (MEA). The morphological alteration of the cathode catalyst layer, particularly the formation of wide and deep cracks is identified as the main reason for the acceleration of water flooding, while degradation of the cathode GDL is minor. This demonstrates that during the long-term operation of DMFCs, the physical disintegration of the cathode catalyst layer is a crucial issue affecting water management, which should be carefully addressed.

Keywords: Direct methanol fuel cell; Membrane electrode assembly; Durability; Catalyst layer cracking; Cathode flooding (search for similar items in EconPapers)
Date: 2014
References: View references in EconPapers View complete reference list from CitEc
Citations: View citations in EconPapers (5)

Downloads: (external link)
http://www.sciencedirect.com/science/article/pii/S030626191400511X
Full text for ScienceDirect subscribers only

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:eee:appene:v:129:y:2014:i:c:p:346-353

Ordering information: This journal article can be ordered from
http://www.elsevier.com/wps/find/journaldescription.cws_home/405891/bibliographic
http://www.elsevier. ... 405891/bibliographic

DOI: 10.1016/j.apenergy.2014.05.016

Access Statistics for this article

Applied Energy is currently edited by J. Yan

More articles in Applied Energy from Elsevier
Bibliographic data for series maintained by Catherine Liu ().