Inequalities in photovoltaics modules reliability: From packaging to PV installation site

Mahmoud Dhimish, Ameer Ahmad and Andy M. Tyrrell

Renewable Energy, 2022, vol. 192, issue C, 805-814

Abstract: In recent years, the determination of the reliability of photovoltaic (PV) modules has been of ubiquitous interest to the PV industry. Therefore, this work reports on the reliability and degradation mechanism of 186 PV modules from packaging to installation stage. The paper shows that no cracks or hotspots affecting the PV modules before the packaging stage, while a minor reduction in the output power was observed at ±0.3%. The same PV modules were delivered using standard practice, and no further precautions were considered. Electroluminescent (EL) images of all PV modules were taken at the PV installation site, and it was discovered that 2.2% evolved cracks. Depending on the crack size, the estimated output power losses under standard test conditions varied from 0.53% to 1.43%. Furthermore, the PV modules were thermally inspected six months after being installed. It was found that hotspots developed in all the cracked PV modules, and their temperature increased from 10 °C to 20 °C. In addition, a potential induced degradation (PID) test was performed on the cracked PV modules and compared with a crack-free module. It was found that PID affected the modules with cracks more than the crack-free module.

Keywords: Solar cells; Cracks; Electroluminescence; Performance analysis; Potential induced degradation (search for similar items in EconPapers)
Date: 2022
References: View references in EconPapers View complete reference list from CitEc
Citations: View citations in EconPapers (4)

Downloads: (external link)
http://www.sciencedirect.com/science/article/pii/S0960148122006243
Full text for ScienceDirect subscribers only

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:eee:renene:v:192:y:2022:i:c:p:805-814

DOI: 10.1016/j.renene.2022.04.156

Access Statistics for this article

Renewable Energy is currently edited by Soteris A. Kalogirou and Paul Christodoulides

More articles in Renewable Energy from Elsevier
Bibliographic data for series maintained by Catherine Liu ().