Gas product behaviour using flower-like nickel-based MOF catalysts for sustainable hydrogen production from biomass

Nowilin James Rubinsin, Wan Nor Roslam Wan Isahak, Salma Samidin, Manoj Pudukudy, Medhat A. Nemitallah and Nabila A. Karim

Renewable Energy, 2025, vol. 246, issue C

Abstract: Biomass pyrolysis offers a promising pathway for converting renewable feedstocks into hydrogen-rich syngas. However, the efficiency of this process depends heavily on the catalyst used. Nickel-based catalysts, while known for their catalytic activity and cost-effectiveness, often face challenges such as deactivation and agglomeration under pyrolysis conditions. To overcome these limitations, this study explores metal-organic frameworks (MOFs) as catalysts, with additional metal promoters to enhance Ni-based systems. Ni-MOF and Ce-Ni-MOF catalysts were synthesized and systematically evaluated, focusing on variables such as catalyst type, temperature, and catalyst-to-biomass ratio. Both catalysts exhibited highly textured, flower-like structures with loosely packed sheets, providing a large surface area for enhanced catalytic reactions. Ni-MOF increased hydrogen production by 96 % (13,785 mL/g, 53.0 vol%) within 10 min compared to non-catalytic conditions. Ce-Ni-MOF showed superior long-term performance, producing 2252 mL/g (44 vol%) of H2 and achieving 66 % and 76 % higher hydrogen yields than Ni-MOF at 20 and 30 min, respectively. Structural analysis revealed that the catalysts’ flower-like morphology remained intact after pyrolysis, with increased porosity suggesting partial evolution of the MOF structure at high temperatures. Ni-MOF exhibited an increase in nickel loading from 39.8 wt% to 59.5 wt% post-pyrolysis, which further enhanced its catalytic activity. Ce-Ni-MOF displayed a narrower particle size distribution (6–11 nm) and improved stability, with nickel loading only slightly decreasing from 20.7 wt% to 18.4 wt%, maintaining uniformity over time. Both catalysts achieved optimal catalytic activity at a 1:1 catalyst-to-biomass ratio, although Ni-MOF experienced a 61 % reduction in H2 production at a 1:4 ratio. Higher temperatures (800 °C) further enhanced hydrogen, CO, and CH4 yields for both catalysts. These findings demonstrate the potential of MOF-based nickel catalysts for advancing renewable hydrogen production, with Ce-Ni-MOF offering enhanced stability and long-term catalytic efficiency under various conditions.

Keywords: Hydrogen; MOF; Nickel; Cerium; Biomass; Pyrolysis (search for similar items in EconPapers)
Date: 2025
References: Add references at CitEc
Citations:

Downloads: (external link)
http://www.sciencedirect.com/science/article/pii/S0960148125005488
Full text for ScienceDirect subscribers only

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:eee:renene:v:246:y:2025:i:c:s0960148125005488

DOI: 10.1016/j.renene.2025.122886

Access Statistics for this article

Renewable Energy is currently edited by Soteris A. Kalogirou and Paul Christodoulides

More articles in Renewable Energy from Elsevier
Bibliographic data for series maintained by Catherine Liu ().