Microstructural optimization and extended durability studies of low-cost rough graphite–aluminium solar absorber surfaces

P. Konttinen and P.D. Lund

Renewable Energy, 2004, vol. 29, issue 6, 823-839

Abstract: Mechanically manufactured low-cost selective inhomogeneous rough graphite–aluminium (C/Al2O3/Al) solar absorber surfaces provide, at the current state of development, solar absorptance α=0.90 and thermal emittance ε=0.22. Based on a literature review, significantly lower emittance values could theoretically be achieved by utilization of surface plasmons in rough surfaces with an optimal graphite layer thickness, groove depth and sinusoidal surface profile periodicity. It is possible that an arbitrary form of roughening could produce equally good optical properties. In order to achieve lower emittance manufacturing parameters, the composition of silicon carbide grinding pad and the corresponding grinding pattern are required to be enhanced. The commercially available grinding pads used so far have not yielded optimal results. An antireflection coating could improve α to >0.90. Absorber samples were subjected to 383 days of temperature and irradiance cycling. In total, the samples were exposed to ultraviolet (UV) irradiation equivalent to 5–15 years of normal outdoor use. The results show that the samples are not sensitive to natural levels of UV irradiation or cycling-induced degradation of optical properties. A clear increment in absorptance was observed after the first 50 days of cycling. The elevated temperature of 130 °C is the probable cause for the increase. Reference samples indicated similar aging behaviour both after 4 years of natural exposure and after relatively short constant temperature tests at 120 and 180 °C.

Keywords: Rough solar absorber surface; C/Al2O3/Al; Mechanical manufacturing; Surface plasmons; Cyclic aging (search for similar items in EconPapers)
Date: 2004
References: View complete reference list from CitEc
Citations: View citations in EconPapers (3)

Downloads: (external link)
http://www.sciencedirect.com/science/article/pii/S0960148103003859
Full text for ScienceDirect subscribers only

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:eee:renene:v:29:y:2004:i:6:p:823-839

DOI: 10.1016/j.renene.2003.11.008

Access Statistics for this article

Renewable Energy is currently edited by Soteris A. Kalogirou and Paul Christodoulides

More articles in Renewable Energy from Elsevier
Bibliographic data for series maintained by Catherine Liu ().