Enhanced supercurrent density in polycrystalline YBa2Cu3O7-δ at 77 K from calcium doping of grain boundaries

G. Hammerl, A. Schmehl, R. R. Schulz, B. Goetz, H. Bielefeldt, C. W. Schneider, H. Hilgenkamp and J. Mannhart ()
Additional contact information
G. Hammerl: Experimental Physics VI, Center for Electronic Correlations and Magnetism, Institute of Physics, University of Augsburg
A. Schmehl: Experimental Physics VI, Center for Electronic Correlations and Magnetism, Institute of Physics, University of Augsburg
R. R. Schulz: Experimental Physics VI, Center for Electronic Correlations and Magnetism, Institute of Physics, University of Augsburg
B. Goetz: Experimental Physics VI, Center for Electronic Correlations and Magnetism, Institute of Physics, University of Augsburg
H. Bielefeldt: Experimental Physics VI, Center for Electronic Correlations and Magnetism, Institute of Physics, University of Augsburg
C. W. Schneider: Experimental Physics VI, Center for Electronic Correlations and Magnetism, Institute of Physics, University of Augsburg
H. Hilgenkamp: Experimental Physics VI, Center for Electronic Correlations and Magnetism, Institute of Physics, University of Augsburg
J. Mannhart: Experimental Physics VI, Center for Electronic Correlations and Magnetism, Institute of Physics, University of Augsburg

Nature, 2000, vol. 407, issue 6801, 162-164

Abstract: Abstract With the discovery of high-temperature superconductivity1, it seemed that the vision of superconducting power cables operating at the boiling point of liquid nitrogen (77 K) was close to realization. But it was soon found that the critical current density Jc of the supercurrents that can pass through these polycrystalline materials without destroying superconductivity is remarkably small1,2. In many materials, Jc is suppressed at grain boundaries2,3,4, by phenomena such as interface charging and bending of the electronic band structure5,6,7,8,9. Partial replacement (‘doping’) of the yttrium in YBa2Cu3O7-δ with calcium has been used to increase grain-boundary Jc values substantially, but only at temperatures much lower than 77 K (ref. 9). Here we show that preferentially overdoping the grain boundaries, relative to the grains themselves, yields values of Jc at 77 K that far exceed previously published values. Our results indicate that grain-boundary doping is a viable approach for producing a practical, cost-effective superconducting power cable operating at liquid-nitrogen temperatures.

Date: 2000
References: Add references at CitEc
Citations:

Downloads: (external link)
https://www.nature.com/articles/35025014 Abstract (text/html)
Access to the full text of the articles in this series is restricted.

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:nat:nature:v:407:y:2000:i:6801:d:10.1038_35025014

Ordering information: This journal article can be ordered from
https://www.nature.com/

DOI: 10.1038/35025014

Access Statistics for this article

Nature is currently edited by Magdalena Skipper

More articles in Nature from Nature
Bibliographic data for series maintained by Sonal Shukla () and Springer Nature Abstracting and Indexing ().