Strongly linked current flow in polycrystalline forms of the superconductor MgB2

D. C. Larbalestier (), L. D. Cooley, M. O. Rikel, A. A. Polyanskii, J. Jiang, S. Patnaik, X. Y. Cai, D. M. Feldmann, A. Gurevich, A. A. Squitieri, M. T. Naus, C. B. Eom, E. E. Hellstrom, R. J. Cava, K. A. Regan, N. Rogado, M. A. Hayward, T. He, J. S. Slusky, P. Khalifah, K. Inumaru and M. Haas
Additional contact information
D. C. Larbalestier: Applied Superconductivity Center, University of Wisconsin–Madison
L. D. Cooley: Applied Superconductivity Center, University of Wisconsin–Madison
M. O. Rikel: Applied Superconductivity Center, University of Wisconsin–Madison
A. A. Polyanskii: Applied Superconductivity Center, University of Wisconsin–Madison
J. Jiang: Applied Superconductivity Center, University of Wisconsin–Madison
S. Patnaik: Applied Superconductivity Center, University of Wisconsin–Madison
X. Y. Cai: Applied Superconductivity Center, University of Wisconsin–Madison
D. M. Feldmann: Applied Superconductivity Center, University of Wisconsin–Madison
A. Gurevich: Applied Superconductivity Center, University of Wisconsin–Madison
A. A. Squitieri: Applied Superconductivity Center, University of Wisconsin–Madison
M. T. Naus: Applied Superconductivity Center, University of Wisconsin–Madison
C. B. Eom: Applied Superconductivity Center, University of Wisconsin–Madison
E. E. Hellstrom: Applied Superconductivity Center, University of Wisconsin–Madison
R. J. Cava: Princeton University
K. A. Regan: Princeton University
N. Rogado: Princeton University
M. A. Hayward: Princeton University
T. He: Princeton University
J. S. Slusky: Princeton University
P. Khalifah: Princeton University
K. Inumaru: Princeton University
M. Haas: Princeton University

Nature, 2001, vol. 410, issue 6825, 186-189

Abstract: Abstract The discovery of superconductivity at 39 K in magnesium diboride1, MgB2, raises many issues, a critical one being whether this material resembles a high-temperature copper oxide superconductor or a low-temperature metallic superconductor in terms of its behaviour in strong magnetic fields. Although the copper oxides exhibit very high transition temperatures, their in-field performance2 is compromized by their large anisotropy, the result of which is to restrict high bulk current densities to a region much less than the full magnetic-field–temperature (H–T) space over which superconductivity is found. Moreover, the weak coupling across grain boundaries makes transport current densities in untextured polycrystalline samples low and strongly sensitive to magnetic field3,4. Here we report that, despite the multiphase, untextured, microscale, subdivided nature of our MgB2 samples, supercurrents flow throughout the material without exhibiting strong sensitivity to weak magnetic fields3. Our combined magnetization, magneto-optical, microscopy and X-ray investigations show that the supercurrent density is mostly determined by flux pinning, rather than by the grain boundary connectivity. Our results therefore suggest that this new superconductor class is not compromized by weak-link problems, a conclusion of significance for practical applications if higher temperature analogues of this compound can be discovered.

Date: 2001
References: Add references at CitEc
Citations:

Downloads: (external link)
https://www.nature.com/articles/35065559 Abstract (text/html)
Access to the full text of the articles in this series is restricted.

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:nat:nature:v:410:y:2001:i:6825:d:10.1038_35065559

Ordering information: This journal article can be ordered from
https://www.nature.com/

DOI: 10.1038/35065559

Access Statistics for this article

Nature is currently edited by Magdalena Skipper

More articles in Nature from Nature
Bibliographic data for series maintained by Sonal Shukla () and Springer Nature Abstracting and Indexing ().