Machine-learning design of ductile FeNiCoAlTa alloys with high strength

Yasir Sohail, Chongle Zhang, Dezhen Xue, Jinyu Zhang (), Dongdong Zhang, Shaohua Gao, Yang Yang, Xiaoxuan Fan, Hang Zhang, Gang Liu, Jun Sun () and En Ma ()
Additional contact information
Yasir Sohail: Xi’an Jiaotong University
Chongle Zhang: Xi’an Jiaotong University
Dezhen Xue: Xi’an Jiaotong University
Jinyu Zhang: Xi’an Jiaotong University
Dongdong Zhang: Xi’an Jiaotong University
Shaohua Gao: Xi’an Jiaotong University
Yang Yang: Xi’an Jiaotong University
Xiaoxuan Fan: Xi’an Jiaotong University
Hang Zhang: Xi’an Jiaotong University
Gang Liu: Xi’an Jiaotong University
Jun Sun: Xi’an Jiaotong University
En Ma: Xi’an Jiaotong University

Nature, 2025, vol. 643, issue 8070, 119-124

Abstract: Abstract The pursuit of strong yet ductile alloys has been ongoing for centuries. However, for all alloys developed thus far, including recent high-entropy alloys, those possessing good tensile ductility rarely approach 2-GPa yield strength at room temperature. The few that do are mostly ultra-strong steels1–3; however, their stress–strain curves exhibit plateaus and serrations because their tensile flow suffers from plastic instability (such as Lüders strains)1–4, and the elongation is pseudo-uniform at best. Here we report that a group of carefully engineered multi-principal-element alloys, with a composition of Fe35Ni29Co21Al12Ta3 designed by means of domain knowledge-informed machine learning, can be processed to reach an unprecedented range of simultaneously high strength and ductility. An example of this synergy delivers 1.8-GPa yield strength combined with 25% truly uniform elongation. We achieved strengthening by pushing microstructural heterogeneities to the extreme through unusually large volume fractions of not only coherent L12 nanoprecipitates but also incoherent B2 microparticles. The latter, being multicomponent with a reduced chemical ordering energy, is a deformable phase that accumulates dislocations inside to help sustain a high strain hardening rate that prolongs uniform elongation.

Date: 2025
References: Add references at CitEc
Citations:

Downloads: (external link)
https://www.nature.com/articles/s41586-025-09160-2 Abstract (text/html)
Access to the full text of the articles in this series is restricted.

Related works:
This item may be available elsewhere in EconPapers: Search for items with the same title.

Export reference: BibTeX RIS (EndNote, ProCite, RefMan) HTML/Text

Persistent link: https://EconPapers.repec.org/RePEc:nat:nature:v:643:y:2025:i:8070:d:10.1038_s41586-025-09160-2

Ordering information: This journal article can be ordered from
https://www.nature.com/

DOI: 10.1038/s41586-025-09160-2

Access Statistics for this article

Nature is currently edited by Magdalena Skipper

More articles in Nature from Nature
Bibliographic data for series maintained by Sonal Shukla () and Springer Nature Abstracting and Indexing ().